Thermal cycling behavior of La2Zr2O7/Yb2Si2O7/SiC coated PIP Cf/SiC composites under burner rig tests

Pengju Chen,Peng Xiao,Zhuan Li,Yang Li,Sian Chen,Junjie Duan,Pingyi Deng
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.02.005
IF: 5.7
2021-07-01
Journal of the European Ceramic Society
Abstract:Ytterbium disilicate (Yb2Si2O7) and lanthanum zirconate (La2Zr2O7) powders were synthesized by solvent gel (sol-gel) method. To improve the oxidation resistance of Cf/SiC composites at high-temperature and high-speed gas scour environment, a tri-layer La2Zr2O7/Yb2Si2O7/SiC EBCs was prepared on the surface of Cf/SiC composites by chemical vapor deposition (CVD) and sol-gel method combined with air spraying. Results show that tri-layer La2Zr2O7/Yb2Si2O7/SiC coating showed better oxidation resistance for Cf/SiC samples than bi-layer Yb2Si2O7/SiC coating, which can efficiently prevent the oxidation of Cf/SiC samples in gas scour environment at 1773 K for 24 thermal cycles (360 min) with a weight loss of 7.06 × 10−3 g cm-2. Microstructure characterization revealed that crack deflection phenomenon in tri-layer coating can largely avoid the formation of penetrating cracks and even improve the oxidation resistance of the coating. After the corrosion of tri-layer coating in high-speed and high-temperature gas, a small amount of coating fell off and eventually formed coating corrosion pit area and coating fracture area.
materials science, ceramics
What problem does this paper attempt to address?
The paper attempts to address the issue of how to improve the oxidation resistance of carbon fiber reinforced silicon carbide composites (Cf/SiC) in high-temperature and high-speed gas erosion environments. Specifically, the researchers designed a three-layer La2Zr2O7/Yb2Si2O7/SiC environmental barrier coating system. The aim is to prepare this coating using a combination of chemical vapor deposition (CVD) and sol-gel methods along with air spraying techniques, to enhance the adaptability and durability of Cf/SiC composites in extreme working environments. The paper evaluates the thermal cycling behavior and oxidation resistance of this novel three-layer coating through burner rig tests and compares it with a double-layer Yb2Si2O7/SiC coating to verify its effectiveness and advantages.