Oxidation properties of tri-layer ytterbium-disilicate/mullite/silicon-carbide environment barrier coatings for Cf/SiC composites

Pengju Chen,Peng Xiao,Zhuan Li,Yang Li,Jinwei Li

DOI: https://doi.org/10.1016/j.surfcoat.2020.126329

IF: 4.865

2020-11-01

Surface and Coatings Technology

Abstract:<p>Mullite (Al₆Si₂O₁₃) and ytterbium disilicate (Yb₂Si₂O₇) powders were synthesized by the solvent gel (sol-gel) method. To improve the oxidation resistance of C_f/SiC composites at high temperatures, a novel tri-layer Yb₂Si₂O₇/Al₆Si₂O₁₃/SiC environment barrier coatings (EBCs) was deposited on the surface of C_f/SiC composites by chemical vapor deposition (CVD) and air spray sol-gel methods. Results show that Yb₂Si₂O₇/Al₆Si₂O₁₃/SiC coating lost its ability to protect C_f/SiC composites in the air environment at 1773 K due to the Yb₂Si₂O₇ particles in Yb₂Si₂O₇ top coating diffused into the Al₆Si₂O₁₃ middle coating, which eventually form a eutectic interface with the extension of oxidation time. However, Yb₂Si₂O₇/Al₆Si₂O₁₃/SiC coating can efficiently prevent the oxidation of C_f/SiC composites at 1673 K for 150 h with a weight loss of 2.69 × 10⁻³ g·cm⁻². The growth of grains and the disappearance of micro-holes in Al₆Si₂O₁₃ and Yb₂Si₂O₇ coatings deposited by air spray sol-gel method led to the excellent oxidation resistance of Yb₂Si₂O₇/Al₆Si₂O₁₃/SiC coating.</p>

physics, applied,materials science, coatings & films

What problem does this paper attempt to address?

This paper attempts to address the issue of rapid oxidation of carbon fiber reinforced silicon carbide composites (C f/SiC) in high-temperature environments. C f/SiC composites are widely used in fields such as gas turbine thermal structural components, rocket nozzles, and heat exchanger parts due to their high-temperature mechanical properties and lightweight characteristics. However, these materials are prone to rapid oxidation in environments rich in air and water vapor, affecting their service life and performance. Therefore, it is necessary to develop environmental barrier coatings (EBCs) to enhance the adaptability of C f/SiC composites to complex high-temperature environments.

To improve the oxidation resistance of C f/SiC composites at high temperatures, the research team designed a novel three-layer environmental barrier coating system, namely ytterbium disilicate/mullite/silicon carbide (Yb₂Si₂O₇/Al₆Si₂O₁₃/SiC) coating. This coating was prepared by chemical vapor deposition (CVD) and air-sprayed sol-gel methods, and its oxidation resistance at high temperatures was studied in detail.

The main findings of the study include:
1. In air at 1773 K, Yb₂Si₂O₇ particles diffuse into the Al₆Si₂O₁₃ coating of the intermediate layer, eventually forming a eutectic interface, causing the coating to lose its protective effect.
2. In air at 1673 K, the Yb₂Si₂O₇/Al₆Si₂O₁₃/SiC coating can effectively prevent the oxidation of C f/SiC composites. After 150 hours, the weight loss of the sample is only 2.69 × 10⁻³ g·cm⁻², with a corresponding weight loss rate of 1.79 × 10⁻⁵ g·cm⁻²·h⁻¹.
3. As the oxidation process progresses, the density of the mullite intermediate layer and the Yb₂Si₂O₇ top layer prepared by the air-sprayed sol-gel method increases, and the number of micropores decreases, thereby improving the oxidation resistance of the coating.

In conclusion, this study proposes a novel three-layer environmental barrier coating system that significantly improves the oxidation resistance of C f/SiC composites at 1673 K, providing a new solution for the application of high-temperature structural materials.