Abstract:A multilayer CrSi2/MoSi2/SiC–Mo2C composite anti-oxidation coating was in-situ prepared on Mo substrate by a three-step pack cementation method. Energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) tests indicated that the coating was composed of CrSi2, MoSi2, SiC and Mo2C. Furthermore, back scattered electron (BSE) and electron probe microanalysis (EPMA) analyses demonstrated that the whole composite coating was about 65μm and the outermost layer was a composite which was composed of CrSi2, MoSi2 and SiC, and just beneath it was a Mo2C transitional layer which connected the outer layer and the substrate Mo. Since the distribution of the elements in the composite coating was gradually increased or decreased and thus no distinguished interface arose during the preparation process. Cyclic oxidation experiments indicated that the mass loss was only 5.01wt.% in 120min at 1600°C for CrSi2/MoSi2/SiC–Mo2C coated samples, which was much lower than that of MoSi2/SiC–Mo2C coated ones. Besides the Si diffusion hindrance effects of Mo2C transitional layer, BSE, surface profilometer and EPMA observations proved that Cr in the form of CrSi2 could not only reduce the mismatch between the coating and the substrate through the formation of Cr2O3, but also accelerate the formation of a mixed protecting oxide scale at low temperature. Moreover, the Cr2O3 in the scale might also stabilize the glassy coating at high temperature by restraining the volatilization of SiO2.

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

ZrSi2-SiC/SiC Anti-Oxidant Coatings Prepared on Graphite Spheres by Two-Step Pack Cementation Process

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

An oxidation protective coating prepared by SiC densifying HfB2-SiC skeleton for SiC-coated C/C composites at 1473, 1773, and 1973 K

Effect of Al2O3 addition on the microstructure and oxidation behavior of SiC coating prepared by pack cementation on C/C composites

Interfacial modification and oxidation resistance behavior of a CVD-SiC coating for C/SiC composites

A carbon nanotube–enhanced SiC coating for the oxidation protection of C/C composite materials

Multi-composition Coating for Oxidation Protection of Modified Carbon-Bonded Carbon Fiber Composites

Improved oxidation and thermal shock resistance of SiC-Si coating with a SiC w /PyC network structure toughened buffer layer

Effect of Mo/Si Ratio on the Microstructure and Oxidation Resistance of Si-Mo Coating for C/C Composites

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites

Effect of the Incorporation of SiC Nanowire with Double Protective Layers on SiC Coating for C/C Composites

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Fabrication of CrSi2/MoSi2/SiC–Mo2C Gradient Composite Coating on Mo Substrate and the Stabilizing Effect of Cr on the Coating's Anti-Oxidation Properties