Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

In situ formation mechanism of spinel-like Al5O6N and plate-like Al7O3N5 in the two-step sintered Al–Al2O3 composites

Effect of Si3N4 mesophase on the formation of Al2OC-AlNss in resin-bonded Al–Al2O3 composites

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

In‐situ synthesis of 15R‐Sialon from Al‐Si 3 N 4 ‐Al 2 O 3 composite at 1500°C via liquid‐phase sintering

Preparation and properties of Al2O3/Ni composite from NiAl2O4 spinel by in situ reaction sintering method

In situ formation mechanism of aluminum oxycarbonitride in the unoxidized zone of Al–Al2O3 composites

In-Situ Reactive Synthesis of AlN-SiC Composites and Solid Solutions

Mechanism of synthesizing Al2O3/Fe-Al composites with nano Al2O3 fibers by in-situ process

In situ reaction mechanism of MgAlON in Al–Al2O3–MgO composites at 1700°C under flowing N2

Impact of structure and flow-path on in situ synthesis of AlN: Dynamic microstructural evolution of Al-AlN-Si materials

In-situ formation of AlN/Al composite

Oxidation mechanism of Al–Si–SiC composite at elevated temperature

Combustion synthesis of AlN-SIC solid solutions

Formation mechanism of Al4SiC4 in Al–SiC composite under flowing nitrogen at 1300 °C

Characteristic and function of the dynamic Al-AlN core-shell structure in Al-Al 2 O 3 composite at elevated temperature

Microstructure and Mechanical Behavior of NixAly–Al2O3 in Situ Composites by Pre-Oxidation Followed by Hot-Pressed Reactive Sintering

Effect of the Starting AlN Content on the Phase Formation and Property of the Novel In-Situ Fabricated X-SiAlON/BN Composites

Preparation, structure, and properties of Cr2N reinforced Al2O3 composites

Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C

In Situ Fabrication and Mechanical Properties of Al–AlN Composite by Hot Extrusion of Partially Nitrided AA6061 Powder