Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Reactive synthesis of alumina-boron nitride composites

In Situ Combustion Synthesis of TiB<sub>2</sub>-AIN Composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Reaction-Bonded Boron Nitride-Aluminum Nitride Ceramic Composites

In-situ formation of AlN/Al composite

Synthesis of h‐BN composite powders via aluminothermic reduction combustion route

High-pressure Synthesis of Al2O3-cBN Composites: Effect of Thermodynamic Condition and Cbn Volume Fraction on Their Microstructure and Properties

Boron Nitride?Aluminum Nitride Ceramic Composites Fabricated by Transient Plastic Phase Processing

Reactive hot-pressing TiB2/AlN ceramic composites

In situ reaction mechanism of MgAlON in Al–Al2O3–MgO composites at 1700°C under flowing N2

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

In situ formation mechanism of spinel-like Al5O6N and plate-like Al7O3N5 in the two-step sintered Al–Al2O3 composites

In-Situ Reactive Synthesis of AlN-SiC Composites and Solid Solutions

Synthesis and characterization of cubic boron nitride (Al)-Al2O3 composites under high pressure and high temperature conditions

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

Preparation of NiAl2O4/Al2O3 composite nanopowder

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Composite Nitride Nanoceramics in the System Titanium Nitride (TiN)-Aluminum Nitride (AlN) through High Pressure and High Temperature Sintering of Synthesis-Mixed Nanocrystalline Powders

In-situ synthesis of Al3BC/Al composites from amorphous boron and graphene nanoplates by solid reaction

Fabrication of machinable AlN–BN composites with high thermal conductivity by pressureless sintering turbostatic BN-coated AlN nanocomposite powders

Synthesis of Oxynitride Composites during Combustion of a Ferrosilicon–Natural Mineral–Aluminum Mixture in Nitrogen