Abstract:Based on the improvement of the phase transition temperature of Ti by Al element and the excellent strengthening effect of TiC particles, this paper selects Ti 2 AlC as the precursor, striving to improve the high-temperature performance of the Ti matrix. The composites with 1–10 vol% Ti 2 AlC addition were fabricated by hot-pressing sintering. And a detailed study was conducted on the reaction process, microstructure, room and high temperature compression properties of the composites. The experimental results show that the separation of Al elements at the A-position occurs at around 700 °C in Ti 2 AlC, and the Al element is homogenized in the matrix during the subsequent sintering process. Micron sized TiC particles are mainly distributed at the Ti grain boundaries, while the content of sub-micron sized TiC particles entering the crystal increases with the increasing Ti 2 AlC addition. The interface mismatch between TiC and Ti is small, and the bonding is well. These microstructures enable composite materials to exhibit excellent mechanical properties, with 10 vol% Ti 2 AlC/Ti composite having a yield strength of 1858 MPa and an ultimate strength of 2200 MPa at room temperature, and maintaining a yield strength of 602 MPa and an ultimate strength of 1264 MPa at 500 °C.

Reactive hot-pressing TiB2/AlN ceramic composites

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Microstructure and Mechanical Properties of TiN–TiB2–hBN Composites Fabricated by Reactive Hot Pressing Using TiN–B Mixture

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

In Situ Combustion Synthesis of TiB<sub>2</sub>-AIN Composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

Fabrication of BN-AlN-TiB2 Compound Conductive Ceramics by Self-Propagating High Temperature Synthesis and Hot Isostatic Pressing

Hot pressing and microstructural characterization of SiC and TiN added TiB2 ceramics

Synthesis of Tin/Alon Composite Ceramics

Design and Strengthening Behaviour of Ti2alc/Tial Composite by Low-Temperature Hot-Pressing Process

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Si3N4/TiN Ceramic Composites Produced by Hot Pressing

Reactive synthesis of alumina-boron nitride composites

Microstructure, Mechanical Properties and Oxidation Behavior of Reactive Hot-Pressed (Zr,Ti)B2-SiC-ZrC Composites

Microstructure and Mechanical Properties of AlN-TiN-TiB2 Composite Conductive Ceramics

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

Self-Propagating High-Temperature Synthesis Pressing of Composites Based on the TiB2–B4C–Al System

TiN/Al_2O_3 Composite Material Synthesized by Aluminothermic Reduction Process in Coke Bed