Abstract:SiC fibers are widely used in composites exposed to high temperature oxidizing environments. The present study compares the oxidation behavior of SiC fibers and the associated changes in tensile strength upon their exposure to dry air and steam for up to 50 hours at temperatures from 950°C to 1350°C. In both cases, the scale thickness and oxide microstructure were analyzed by scanning electron microscopy. When the SiC fibers were oxidized in air, a crack-free amorphous oxide layer formed at temperatures up to 1200°C, whereas a cracked, crystallized oxide layer was found at 1350°C. By contrast under steam environment, a crystalline oxide forms at 950°C for oxidation times longer than 30 h. In both environments, the fiber strength decreased with increasing exposure time and temperature, the degradation being faster after oxidation in steam compared to dry air. This appears to relate to residual stress in the oxide scale and a reduction in the cross section of the load-bearing unoxidized SiC. An increase in defect size may also contribute to the loss of strength. The oxide scale follows parabolic growth kinetics in both dry air and in steam from 950°C to 1350°C, except at 1350°C for over 30 hours. The oxidation rate in steam is faster than that in dry air, with activation energies of 79.8±1.4 kJ/mol in steam and 153.6±3.4 kJ/mol in air, respectively. This work is relevant to the application of SiC fibers and SiC fiber reinforced composites in air and steam environments at high temperature.

Oxidation resistance of SiCf/SiC composites with a PyC/SiC multilayer interface at 500 °C to 1100°C

Effects of pyrolysis temperatures on the oxidation behavior of PIP-processed SiCf/SiC composites

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

Mechanical properties and strengthening mechanism of SiCf/SiC mini-composites modified by SiC nanowires

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Anti-oxidation performance of mini SiC/SiC composites containing ZrSiO 4 multilayer interphase

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Oxidation Behavior of SiCf/SiC Composites Modified by Layered-Y2Si2O7 in Wet Oxygen Environment

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Microstructural evolution and oxide layer structure of Csf/SiBCN composites during oxidation at 1500 °C

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

High-temperature tensile behavior of 3D SiC/SiC composites

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam