Abstract:Direct fabrication of uniform patterns of Fe2O3 center dot xH(2)O nanoparticles on the SiOx/Si surface was achieved by microcontact printing (mu CP). The as-prepared poly( dimethylsiloxane) ( PDMS) stamps with a hydrophobic surface were used. The "ink" was an FeCl3 center dot 6H(2)O ethanol solution. Fe2O3 center dot xH(2)O nanoparticles were formed on the stamps from the hydrolysis of FeCl3 during the ink drying process and were then directly deposited onto the SiOx/Si surface with mu CP. The nanoparticles were transferred to the areas beneath the "raised" portions of the stamp at low ink concentration but populated at the areas beneath the "recessed" portions of the stamp at high ink concentration. The hydrophobic property of the stamp surface cooperated with the gravity of the particles in bringing on such an exchange of recession and repousse. The density and size of the formed nanoparticles could be tuned by varying the ink concentration. The patterned Fe2O3 center dot xH(2)O nanoparticles were used as the catalysts for the growth of single-walled carbon nanotubes (SWCNTs) by CVD. By skillfully patterning the inks of different concentrations on the same SiOx/Si wafer, we studied the effect of the ink concentration on the growth of SWCNTs. It is also shown that this simple method could be extended to the fabrication of other metal-containing nanoparticles.

Study on the formation of circular patterns of α-Fe_2O_3 nanoparticles via chemical vapor deposition with water and ferrocene

Self-Assembled Patterns Of Iron Oxide Nanoparticles By Hydrothermal Chemical-Vapor Deposition

Synthesis and self-organization of γ-Fe2O3 nanoparticles by hydrothermal chemical vapor deposition

Direct Preparation and Patterning of Iron Oxide Nanoparticles Via Microcontact Printing on Silicon Wafers for the Growth of Single-Walled Carbon Nanotubes

Buliding microstructures of organized carbon nanotubes by chemical vapor deposition

Macroscopic Three-Dimensional Arrays of Fe Nanoparticles Supported in Aligned Carbon Nanotubes

Fabrication of superparamagnetic macroporous Fe3O4 and its derivates using colloidal crystals as templates

Controllable Synthesis Of Hollow Alpha-Fe2o3 Nanostructures, Their Growth Mechanism, And The Morphology-Reserved Conversion To Magnetic Fe3o4/C Nanocomposites

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

Preparation of Magnetic Fe3O4/SiO2 Nano-composite Particles by Chemical Deposition in Aqueous Solution

Controlled Synthesis of Porous FeCO3 Microspheres and the Conversion to Α-Fe2o3 with Unconventional Morphology

Controlled Evaporative Self-Assembly of Fe3O4 Nanoparticles Assisted by an External Magnetic Field

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Rapid Synthesis of Fe/SiO2 Catalysts and Growth of Carbon Nanotubes by Chemical Vapor Deposition

Patterned Growth of Well-aligned Carbon Nanotube Arrays on Quartz Substrates by Chemical Vapor Deposition

The Formation of Recumbent Bamboo-Like Carbon Nanotube Patterns on a Patterned Gold Substrate by Chemical Vapor Deposition

Controllable synthesis and characterization of porous FeVO4 nanorods and nanoparticles

Growth of multi-walled carbon nanotubes on Si substrate with Fe3O4/DR film as catalyst precursors

Synthesis, Optical and Magnetic Properties of Α-Fe2o3 Nanoparticles with Various Shapes

The formation of a layer of Fe3O4 nanoplates between two carbon films

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles