Abstract:This paper describes a facile approach to the site-specific growth of single-walled carbon nanombes (SWNTs) on silicon surfaces by chemical vapor deposition (CVD). The approach is based on the use of a surfactant as a resist to define patterns of silicon oxide nanodomains onto which nanoparticles of iron hydroxide (Fe(OH)A 1-5 nm diameter, could be deposited. In base growth mode, the SWNTs can grow from the oxide nanodomains. By controlling the location of oxide nanodomains, site-specific growth could be obtained. The iron hydroxide nanoparticles were prepared by hydrolysis of ferric chloride (FeCl3). Patterned hydroxylated silicon oxide nanodomains were created by scanning probe oxidation (SPO) of silicon substrates modified with aminopropyltrimethoxysilane (APTMS, H2N(CH2)(3)Si(OCH3)(3)). Due to electrostatic interaction, Fe(OH)(3) nanoparticles can be selectively deposited on hydroxyl groups present on silicon oxide nanodomains. To inhibit the assembly of the nanoparticles on a APTMS-coated silicon surface, sodium dodecyl sulfate (SDS) was introduced, which restricted deposition to the hydroxylated nanodomains. A model mechanism for. the selective deposition mechanism has been proposed. It was possible to convert the patterned Fe(OH)3 nanoparticles to iron oxide, which served as a catalyst for the site-specific growth of SWNTs. Raman spectroscopy and AFM were used to characterize the nanotubes on the Si substrate. This will offer the possibility for future integration with conventional microelectronics as well as the development of novel devices.

Direct Preparation and Patterning of Iron Oxide Nanoparticles Via Microcontact Printing on Silicon Wafers for the Growth of Single-Walled Carbon Nanotubes

Patterning Nanoparticles by Microcontact Printing and Further Growth of One-Dimensional Nanomaterials

Patterned carbon nanotubes fabricated by the combination of microcontact printing and diblock copolymer micelles.

Surfactant-resisted assembly of Fe-containing nanoparticles for site-specific growth of SWNTs on Si surface.

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Controllable patterning and CVD growth of isolated carbon nanotubes with direct parallel writing of catalyst using Dip Pen Nanolithography

Selective Growth of Carbon Nanotube on Silicon Substrates

Site-specific Forest-assembly of Single-Wall Carbon Nanotubes on Electron-beam Patterned SiOx/Si Substrates

Discrete Growth of Single-walled Carbon Nanotubes on Surfaces

Growth of multi-walled carbon nanotubes on Si substrate with Fe3O4/DR film as catalyst precursors

Synthesis of Locally-Ordered Carbon Nanotube Arrays from Patterned Catalyst by Self-Assembly Technique

Controllable fabrication of carbon nanotubes on catalysts derived from PS-b-P2VP block copolymer template and in situ synthesis of carbon nanotubes/Au nanoparticles composite materials

High-Density Growth of Single-Wall Carbon Nanotubes on Silicon by Fabrication of Nanosized Catalyst Thin Films

Controlling the Diameter of Single-Walled Carbon Nanotubes by Improving the Dispersion of the Uniform Catalyst Nanoparticles on Substrate

Direct Growth of Three-Dimensional Multicomponent Micropatterns of Vertically Aligned Single-Walled Carbon Nanotubes Interposed with Their Multi-Walled Counterparts on Al-Activated Iron Substrates

Precise arrangement of metal atoms at the interface by a thermal printing strategy

SiO2-promoted growth of single-walled carbon nanotubes on an alumina supported catalyst

Large Area Nanoscale Patterning of Functional Materials Using Organosilicate ink based Nanotransfer Printing

Diameter controlled growth of single-walled carbon nanotubes from SiO2 nanoparticles

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Self-Assembled Patterns Of Iron Oxide Nanoparticles By Hydrothermal Chemical-Vapor Deposition