Abstract:With Y(DPM)(3) and Zr(DPM)(4) as precursors, yttria-stabilized zirconia (YSZ) thin films were deposited onto NiO-SDC substrates using a modified aerosol-assisted metal-organic chemical vapor deposition (AAMOCVD) apparatus, where high power halogen lights were used as assisted heaters. Cubic structured YSZ was obtained when the films were deposited at 650 degrees C. The cubic YSZ transformed to tetragonal structure after annealed at 1100 degrees C for 3 h, possibly due to crystallite growth. Y/Zr mole ratio of the deposited film depends on the Y/Zr ratio of the precursors, indicating that the thin film composition can be effectively controlled. Scanning electron microscopy (SEM) analysis showed a strong bonding between the films and substrates. Thickness of the film was estimated to be about 9 mu m with a high growth rate of 50 nm/min, which inferring the AAMOCVD is very effective in synthesis of YSZ films. AC impedance analyses showed that the ionic conductivity of the YSZ film is 0.034 S/cm at 800 degrees C, which is slightly less than that of bulk YSZ, and the conduction activation energy (E-a) changed from 80.8 kJ/mol to 138.8 kJ/mol at 640 degrees C with decreasing temperature. (c) 2006 Elsevier B.V. All rights reserved.

Fabrication of P‐type Li‐Doped ZnO Films by RF Magnetron Sputtering

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Fabrication of P-Type Li-Doped Zno Films by Pulsed Laser Deposition

Fabrication of P-Type ZnMgO Films Via Pulsed Laser Deposition Method by Using Li As Dopant Source

Realization of p-type ZnO films via monodoping of Li acceptor

Fabrication of P-Type ZnO Thin Films Via DC Reactive Magnetron Sputtering by Using Na As the Dopant Source

P-Type ZnO Thin Films Fabricated by Dc Magnetron Reactive Sputtering Method at Different Substrate Temperatures

Fabrication and Post-Anneal Activation of P-Type ZnMgO:Li Film Using Dc Reactive Magnetron Sputtering

Dopant Source Choice for Formation of P-Type ZnO: Li Acceptor

PLD Growth of p-Type ZnMgO Films with Li-Doped

Fabrication and Characteristics of the Low-Resistive P-Type ZnO Thin Films by DC Reactive Magnetron Sputtering

Preparation and Properties of P-Type Ag-doped ZnMgO Thin Films by Pulsed Laser Deposition

Preparation and Characteristics of P-Type Zno Films by Dc Reactive Magnetron Sputtering

Effect of Oxygen Pressure on Structural and Electrical Properties of Pulsed Laser Deposition-Derived Zn0.95mg0.05o: Li Thin Films

A Facile Route to Realize P-Type ZnO Thin Films Via Li–F Codoping: Experiments and Theory

Low-resistivity, Stable P-Type ZnO Thin Films Realized Using a Li–N Dual-Acceptor Doping Method

Fabrication of p-type ZnO thin films via MOCVD method by using phosphorus as dopant source

Fabrication of p-type ZnMgO codoped with Al and N using dc reactive magnetron sputtering

Optical and Electrical Properties of N-doped ZnO and Fabrication of Thin-Film Transistors

Fabrication of Sb-Doped P-Type Zno Thin Films by Pulsed Laser Deposition

Fabrication of Lithium-Doped Zinc Oxide Film by Anodic Oxidation and Its Ferroelectric Behavior