Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

The low temperature preparation of nanocrystalline MgAl2O4 spinel by citrate sol–gel process

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

The low temperature fabrication of nanocrystalline MgAl2O4 spinel aerogel by a non-alkoxide sol-gel route

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

A novel method for the synthesis of nano-sized BaAl2O4 with thermal stability

Preparation and Crystallization of Si-Al Gel

Preparation of Magnesium Aluminate Spinel Nanofibers with High Temperature Resistance by Electrospinning Process Based on Non-Hydrolytic Sol-Gel Method

Low Temperature Synthesis of Vanadium Pentoxide Nanocrystallines by Sol-Gel Method

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Preparation of nano-sized SrAl2O4 using an amorphous hetero-nucleus complex as a precursor

Effect of Synthetic Parameters on Synthesis of Magnesium Aluminum Spinels

Facile sol-gel synthesis of ZnAl2O4 spinel nanoceramics for photocatalytic applications: H2 production and MB dye degradation

Novel Synthesis of High Surface Area MgAl2O4 Spinel As Catalyst Support

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Low-temperature Synthesis of Nano-Crystalline Magnesium Titanate Materials by the Sol–gel Method

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Effects of chelation reactions between metal alkoxide and acetylacetone on the preparation of MgAl2O4 powders by sol-gel process

Synthesis of ultrafine MgAl2O4 powders by sol-gel auto ignition

Self-Propagating High-Temperature Synthesis of Magnesium Aluminate Spinel Using Mg–Al Alloy