Abstract:The general preparation method for V2O5 is ammonium salt vanadium precipitation, which inevitably produces large amounts of ammonia nitrogen wastewater. In this paper, we propose an environmentally friendly method for preparing high-purity V2O5 with low ammonium consumption. The purity of the V2O5 product reaches more than 99% while reducing the level of ammonium consumption. The vanadium precipitation efficiency reaches 99.23% and the V2O5 purity of the product reaches 99.05% under the following conditions: precipitation time of 1.5 h, precipitation temperature of 98 °C, initial precipitation pH of 2, ammonium addition coefficient of 2, purification time of 5 min with purification performed twice, purification temperature of 65 °C. In this study, compared with the use of ammonia spirit for vanadium precipitation and ammonium salt vanadium precipitation, the ammonia consumption levels are reduced by 79.80% and 80.00%, and the purity levels are increased by 0.70% and 1.01%, respectively. The compositions of the precipitated (NaV3O8∙xH2O) and purified ((NH4)2V6O16·1.5H2O) hydrolysis products are characterized via XRD. The TGA results show that NaV3O8∙xH2O contains 1.5 times the amount of crystal water. The FTIR results explain that the two V3O8− layers are combined end-to-end to form a V6O162− layer. The change of the product image indicates that the purification process includes three stages. Firstly, heating and NH4+ attack expand the V3O8− layer. NH4+ diffuses more easily into the V3O8− layer. Secondly, NH4+ destroys the electrostatic interaction between Na+ with the V3O8− layer and replacing Na+. Finally, V3O8− is polymerized into V6O162− to keep the crystal structure stable.

Low Temperature Synthesis of Vanadium Pentoxide Nanocrystallines by Sol-Gel Method

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Effects of Preparation Parameters on Room Temperature Formation of Vanadium-Doped Tio2 Nanocrystalline Powder

Synthesis of Single-Crystal Vanadium Dioxide Nanosheets by the Hydrothermal Process

Low temperature synthesis of visible light-driven vanadium doped titania photocatalyst

Preparation, Formation Mechanism of V3O7·H2O Single-Crystal Nanobelts

The Structure and Electrochemical Performance of V2O5 Powder Prepared by Hydrothermal Synthesis at Various Acidification Conditions

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

One-pot Hydrothermal Synthesis of Vanadium Dioxide Nanoparticles

Hydrothermal Preparation of Long Nanowires of Vanadium Oxide

Synthesis of Li1+xV3O8 by Citrate Sol–gel Route at Low Temperature

Low-temperature Synthesis of Bi4Ti3O12 Nanocrystals by Hydrothermal Method

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

A Sustainable Technique to Prepare High-Purity Vanadium Pentoxide via Purification with Low Ammonium Consumption

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

Vanadium Pentoxide Nanobelts and Nanorolls: from Controllable Synthesis to Investigation of Their Electrochemical Properties and Photocatalytic Activities

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Size- and Shape-Controlled Synthesis of Monodisperse Vanadium Dioxide Nanocrystals.

Vanadium Pentoxide Nanowires: Hydrothermal Synthesis, Formation Mechanism, And Phase Control Parameters

A liquid approach for the synthesis of M phase VO2 nanocrystals: Facile synthesis, characterization and reaction mechanism