Abstract:Magnesium aluminate spinel (MgAl2O4) ceramics are high-performance and carbon-free materials widely used in both military and civilian fields. However, it is usually challenging to densify during the solid-state sintering process. The excellent properties of some rare earth oxides have been proved to promote the densification of MgAl2O4 spinel ceramics. But the mechanism of promoting sintering is not clear. In the present work, MgAl2O4 spinel ceramics have been successfully fabricated by co-doping CeO2 and La2O3 via a single-stage solid-state reaction sintering. The effects of addition amounts of CeO2 and La2O3 on phase compositions, microstructures, sintering characteristics, cold compressive strength, and thermal shock resistance of as-prepared MgAl2O4 spinel ceramics were systematically investigated. The results show that by co-doping CeO2 and La2O3 can increase the defect concentration due to the lattice distortion. This could promote the movement of Al3+ and Mg2+ at high temperature, which is beneficial to the formation of more secondary MgAl2O4 spinel. t-ZrO2 with more Ce4+ filling between spinel grains could prevent the growth of grains and promote the densification, besides the new-formed LaAlO3 that was mainly distributed along the grain boundary of the MgAl2O4 phase, both of which were favorable for the formation of dense microstructure of MgAl2O4 spinel materials. At the same time, the formation of more secondary MgAl2O4 spinel and sintering densification also improve the mechanical properties of spinel ceramics. La3+ will segregate to the spinel grain boundary, preventing grain boundary movement and absorbing the main crack's fracture energy. With 3 wt% CeO2 and 3 wt% La2O3 co-doping, the bulk density of the sample increased from 3.02 g∙cm−3 to 3.55 g∙cm−3; the apparent porosity decreased from 12.21% to 9.97%; the cold compressive strength increased from 172.88 MPa to 189.54 MPa; and the residual strength retention ratio after thermal shock increased from 84.92% to 89.15%.

Effects of chelation reactions between metal alkoxide and acetylacetone on the preparation of MgAl2O4 powders by sol-gel process

Hydrolysis Process and Mechanism of Magnesium Aluminate Alkoxides

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

Effect of Synthetic Parameters on Synthesis of Magnesium Aluminum Spinels

Study of Preparation of Cobalt Aluminate by Sol-Gel Process and Electroless Plating

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis of MgAl2O4Spinel Nanometer Powder Via Biology Polysaccharide Assisted Sol-Gel Process

Effect of the citrate sol–gel synthesis on the formation of MgAl2O4 ultrafine powder

Effect of Al2O3 on Sintering and Thermal Shock Resistance of MgO Ceramic

Preparation of Alumina Ultrafine Powders Through Acrylamide, Starch and Glutaric Dialdehyde Mediated Sol–gel Method

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods

Synthesis of magnesium aluminate spinel by reaction sintering with different magnesia sources

Microstructural and Optical Properties of MgAl2O4 Spinel: Effects of Mechanical Activation, Y2O3 and Graphene Additions

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Sol–gel Preparation of Hierarchically Porous Magnesium Aluminate (mgal2o4) Spinel Monoliths for Dye Adsorption

Study on Synthesis of CA6 and MgAl2O4 with Dolomite As a Source of Calcium and Magnesium

Preparation and properties of MgAl2O4 spinel ceramics by double-doped CeO2 and La2O3

Effect of Magnesium Oxide on Preparation of Mullite Fibers Via Sol-Gel Method

Synthesis of ultrafine MgAl2O4 powders by sol-gel auto ignition

Effects of Preparation Conditions on Alkali-Activation Reactivity of Chemosynthetic Al<sub>2</sub>O<sub>3</sub>-2SiO<sub>2</sub> Powders

Polyol-mediated synthesis and characterization of magnesium–aluminum spinel nanoparticles