Abstract:Mesoporous metal oxides with wide pore size, high surface area, and uniform porous structures have demonstrated excellent advantages in various fields. However, the state-of-art synthesis approaches are dominated by wet chemistry, accompanied by use of excessive solvent, and the requirement of time-consuming drying process. Herein, we report a mechanochemical solid-state route to synthesize mesoporous Al2O3 (meso-Al2O3) via aluminum isopropoxide-copolymers assembly. The obtained meso-Al2O3 shows a record high surface area (similar to 644 m(2) g(-1)) and narrow pore size distribution (centered at similar to 5 nm). Moreover, a mechanochemical nonhydrolytic sol-gel strategy is introduced to fabricate mesoporous metal (Cu, Co, Mn, Fe, Mg, Ni)-aluminum binary oxide by using anhydrous metal chlorides and aluminum isopropoxide interplay. More importantly, four or five metals-aluminum oxide complexes with abundant mesopores and single cubic crystalline phase known as high-entropy ceramics are produced. To the best of our knowledge, mesoporous high-entropy metal oxides have not been prepared before, because the high crystallization temperature would make mesopores collapse. Additionally, this high-entropy property endows (CuNiFeCoMg)O-x-Al2O3 with superior SO2-resisting performance (1000 ppm of SO2 in N-2 at 280 degrees C) in the catalytic oxidation of CO compared to single CuO-Al2O3.

Preparation of Porous ZnAl2O4 Spinel Monoliths Through Sol-Gel Route Accompanied with Phase Separation

Synthesis and Characterization of Monolithic ZnAl2O4 Spinel with Well-Defined Hierarchical Pore Structures Via a Sol-Gel Route

Preparation of Li-doped ZrO2 Porous Monoliths via Sol-Gel Process Accompanied by Phase Separation

Preparation of Macroporous Zirconia Monoliths via Sol-Gel Process Accompanied by Phase Separation

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

A General Propylene Epoxide-assisted Sol-Gel Route for the Synthesis of ZrO2-SnO2 Composite Sols

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Preparation of Porous YSZ Monoliths via Sol-gel Process Accompanied by Phase Separation

Preparation of Macroporous Transition Metal Hydroxide Monoliths Via a Sol-Gel Process Accompanied by Phase Separation

Preparation of a Hierarchically Porous AlPO4monolith Via an Epoxide-Mediated Sol–gel Process Accompanied by Phase Separation

Preparation of macroporous zirconia monoliths from ionic precursors via an epoxide-mediated sol-gel process accompanied by phase separation

Preparation of Zirconia Powders by Sol-gel Process

Preparation and Characterization of Macroporous Mayenite Monoliths

Preparation of macroporous Li2ZrO3 monoliths via an epoxide-mediated sol–gel process accompanied by phase separation

Preparation and characterization of ZnO-B2O3-SO2 by sol-gel method

Sol–gel Preparation of Hierarchically Porous Magnesium Aluminate (mgal2o4) Spinel Monoliths for Dye Adsorption

Synthesis and Characterization of Porous Magnesium Aluminate Spinel by Hydrothermal Process

Macroporous MgO Monoliths Prepared by Sol–gel Process with Phase Separation

Hydrothermal Treatment of Macroporous ZrO2 Monoliths

Macroporous Sio2 Monoliths Prepared Via Sol-Gel Process Accompanied by Phase Separation