Mechanical and Thermal Properties of 99% and 92% Alumina at Cryogenic Temperatures

Zhipeng Xie,Weijiang Xue,Haibo Chen,Yong Huang

DOI: https://doi.org/10.1016/j.ceramint.2011.03.066

IF: 5.532

2011-01-01

Ceramics International

Abstract:In the present paper, mechanical properties with respect to bending strength and fracture toughness of 99% and 92% Al2O3 at ambient and cryogenic temperatures (293K, 195K and 77K) were measured with four-point bending method and SENB method respectively. It shows that the bending strength of both 99% and 92% Al2O3 seemed not to depend on temperature and with decreasing temperature there was a slight increase in the fracture toughness of 99% Al2O3 at 77K but that of 92% Al2O3 remained almost unchanged with measurement uncertainties taken into account. It was also discovered that the reduction in the fracture toughness of glass phases in grain boundary had a negative effect on the improvement in that of α-Al2O3, thus the resultant toughness at 77K appears not to increase as 99% Al2O3 does. On basis of qualitative analysis of phase compositions by XRD, the decrease in temperature down to 77K did not result in any phase transformation of which the cryogenic mechanical properties are independent. The thermal conductivity of 99% and 92% Al2O3 was 4.1W/(mK) and 1.7W/(mK) at 20K, respectively, much lower than that of stainless steel. Simultaneously alumina, whose thermal expansion is low between 123K and 170K, can be stable enough to temperature changes. Alumina ceramics, therefore, can be candidate materials for cryogenic application.