Abstract:In this study, the continuous alumina fibers reinforced alumina matrix (Al2O3/Al2O3) composites were fabricated through sol–gel method at a sintering temperature range of 900–1400 °C, and their mechanical properties were analyzed separately. To explore the effects of sintering temperature on mechanical properties of composites, the high temperature properties of fibers and matrix were studied in a comprehensive manner. Our results suggested that the composites fabricated at different temperatures exhibited two different fracture features (ductile fracture and brittle fracture). Besides, the 1100 °C fabricated composites possessed the highest flexural strength of nearly 150 MPa. Al2O3 fibers displayed excellent thermal stability, and did not undergo phase transition during the preparation process. However, the grain size of fibers increased dramatically at a sintering temperature of 1200 °C, which led to a significant decrease in the mechanical properties. In the meantime, the surface morphology of fibers became very uneven because of grain coarsening. Due to the phase transition from γ-Al2O3 to α-Al2O3 at 1200 °C, the elastic modulus and microhardness of matrix increased significantly. The higher sintering temperature not only intensified the matrix but also strengthened the interface bonding, thus making the composites prone to brittle fracture. In conclusion, the optimal temperature of composites preparation should be lower than 1200 °C.

Insight into the high temperature performances of alumina foams

The effect of sintering temperatures on alumina foam strength

High temperature and mesostructure effect on aluminum foam compression responses

Strength degradation of alumina fiber: Irreversible phase transition after high-temperature treatment

Novel silica-modified boehmite aerogels and fiber-reinforced insulation composites with ultra-high thermal stability and low thermal conductivity

High Temperature Thermal Physical Properties of High-Alumina Fibrous Insulation

Effect of heat‐treatment on the microstructure and room‐temperature mechanical properties of alumina–silica fiber

Effects of sintering temperature on mechanical properties of alumina fiber reinforced alumina matrix composites

Alumina-Doped Silica Aerogels for High-Temperature Thermal Insulation

Research of Mechanical and Thermal Properties of Al2O3 at Cryogenic Temperatures

Opacifier embedded and fiber reinforced alumina-based aerogel composites for ultra-high temperature thermal insulation

Effect of high temperature annealing on microstructure and mechanical properties of Morlion735 alumina fiber

High-temperature properties of Al 2 O 3 /SiO 2 composites

Effect of thermal exposure on the microstructure and strength of an alumina‐silica ceramic fiber

High-strength porous alumina ceramics prepared from stable wet foams

Effect of Sintering Temperature on Microstructure and Mechanical Behavior of Alumina-Based Ceramic Shell by SLS

Effect of trace alumina on mechanical, dielectric, and ablation properties of fused silica ceramics

Evolution of the microstructure and mechanical properties of stereolithography formed alumina cores sintered in vacuum

Mechanical and Thermal Properties of 99% and 92% Alumina at Cryogenic Temperatures

Preparation of High Purity Alumina Ceramic Supports at Low Temperature

Preparation and properties of high-purity porous alumina support at low sintering temperature