Abstract:In the present paper, mechanical properties with respect to bending strength and fracture toughness of 99% and 92% Al2O3 at ambient and cryogenic temperatures (293K, 195K and 77K) were measured with four-point bending method and SENB method respectively. It shows that the bending strength of both 99% and 92% Al2O3 seemed not to depend on temperature and with decreasing temperature there was a slight increase in the fracture toughness of 99% Al2O3 at 77K but that of 92% Al2O3 remained almost unchanged with measurement uncertainties taken into account. It was also discovered that the reduction in the fracture toughness of glass phases in grain boundary had a negative effect on the improvement in that of α-Al2O3, thus the resultant toughness at 77K appears not to increase as 99% Al2O3 does. On basis of qualitative analysis of phase compositions by XRD, the decrease in temperature down to 77K did not result in any phase transformation of which the cryogenic mechanical properties are independent. The thermal conductivity of 99% and 92% Al2O3 was 4.1W/(mK) and 1.7W/(mK) at 20K, respectively, much lower than that of stainless steel. Simultaneously alumina, whose thermal expansion is low between 123K and 170K, can be stable enough to temperature changes. Alumina ceramics, therefore, can be candidate materials for cryogenic application.

Research of Mechanical and Thermal Properties of SiC at Cryogenic Temperatures

Si3N4-SiCw composites as structural materials for cryogenic application

Enhanced Mechanical Properties of SiC/Al Composites at Cryogenic Temperatures

Research into Mechanical Properties of Reaction-Bonded Sic Composites at Cryogenic Temperatures

Role of Cryogenic Temperature on the Strengthening Mechanism of Sicw-Al2o3 Composites

Enhanced fracture toughness of silicon nitride ceramics at cryogenic temperatures

Enhanced toughness and hardness at cryogenic temperatures of silicon carbide sintered by SPS

How Does Pore-Induced Crack Change As Temperatures Decrease from 293 K to 77 K?

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

Mechanical and Thermal Properties of 99% and 92% Alumina at Cryogenic Temperatures

Strengthening Mechanism of Aluminum Nitride Ceramics from 293 to 77 K

How Does Crack Bridging Change at Cryogenic Temperatures?

Research of Mechanical and Thermal Properties of Al2O3 at Cryogenic Temperatures

Mechanical and thermal properties of Al 2O 3-ZrO 2 composite ceramics at cryogenic temperatures

Molecular dynamics simulation of the temperature effect on ideal mechanical properties of SiC/BN interface for SiCf/SiC composites

Slow Crack Growth Behavior of Silicon Nitride Ceramics in Cryogenic Environment

Mechanical Properties of Si3N4/BN Fibrous Monolithic Ceramics at Elevated-Temperature

The cryogenic mechanical properties of translucent alumina

Cryogenic and high temperature performance of 4H-SiC power MOSFETs

Enhanced Mechanical Properties of Machinable Mica Glass Ceramics at Cryogenic Temperatures

Bending and Thermal Expansion Properties of 2.5D C/SiC Composites