Abstract:Silicon nitride materials doped with 6wt% ytterbium oxide and 2wt% alumina were prepared by nitro-gen gas pressure sintering.The high temperature dynamic fatigue behavior of the Si_3N_4 composites was investigated in terms of the loading rate dependence of fatigue strength at high temperatures.The specimens were pre-cracked by Vickers indentation to avoid creep and to ensure slow crack growth dominating in fatigue damage.The tests were performed in the four-point bending mode in air at the temperature of 1000℃,1200℃,1300℃ and 1400℃ respectively.The cross head speeds were chosen of 1,0.5,0.1 and 0.01 mm/min at each temperature.By plotting fatigue strength against cross-head speed in double logarithm coordinates,the highest slow crack exponent number N was found in the test at 1200℃,indicating that the critical crack growth was the slowest at this temperature.X-ray (diffraction) and transmission electron microscopy show that the grain boundary crystallization and crack healing(inhibit the) crack growth thus increasing the slow crack growth exponent number.Energy dispersive spectrum(reveals) that the crack surface oxidation may benefit the crystallization at 1200℃,while slow crack growth may be promoted at higher temperatures because of over-oxidation.

Slow Crack Growth Behavior of Silicon Nitride Ceramics in Cryogenic Environment

How Does Crack Bridging Change at Cryogenic Temperatures?

Enhanced fracture toughness of silicon nitride ceramics at cryogenic temperatures

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

How Does Pore-Induced Crack Change As Temperatures Decrease from 293 K to 77 K?

Slow Crack Growth Behavior of 3Y-TZP in Cryogenic Environment Using Dynamic Fatigue and Indentation Technique

Crack propagation in silicon nitride ceramics under various temperatures and grain boundary toughness

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Fracture Toughness of Aluminum Nitride Ceramics at Cryogenic Temperatures

Crack Bridging in Silicon Nitride Ceramics at Various Temperatures and Grain Boundary Toughness

Si3N4-SiCw composites as structural materials for cryogenic application

Enhanced toughness and hardness at cryogenic temperatures of silicon carbide sintered by SPS

The Dynamic Fatigue Behavior of Si<sub>3</sub>N<sub>4</sub> at Different Temperatures

Crystallization Behavior of Amorphous Si2bc3n Ceramic Monolith Subjected to High Pressure

Microstructure and Crack Resistance Behaviour of Silicon Nitride Ceramics

The Dynamic Fatigue Behavior of Si3N4 at Different Temperatures

High-temperature Fatigue Behavior in Pre-Cracked Silicon Nitride Composites Doped with Ytterbium Oxide

Strengthening Mechanism of Aluminum Nitride Ceramics from 293 to 77 K

Effects of microstructures on the fracture properties of silicon nitride ceramics at elevated temperatures

Transient Thermal Shock Behavior Simulation of Porous Silicon Nitride Ceramics

Porosity and Oxide Layer Dependence of Thermal Shock Behavior of Porous Silicon Nitride Ceramics