Abstract:Cr2AlB2 and Cr4AlB4 are members of the MAB phases that exhibit unique properties of both metals and ceramics. However, despite these unique characteristics, Cr2AlB2 and Cr4AlB4 phase coatings have not been widely investigated. In this study, Cr2AlB2 and Cr4AlB4 MAB phase coatings were fabricated by magnetron sputtering at room temperature and post-annealing. A composite target, consisting of a phase-pure disc-shaped CrB target overlapped by uniformly dispersed fan-shaped Al slices, was placed parallel to the substrates. The Al content of the coatings was adjusted by altering the areal proportion of the Al slices. MAB phases have crystallized upon post-annealing the as-deposited coatings on Al2O3(0001) substrates in Ar. The phase compositions and morphologies of the crystalline coatings were found to be dependent on the Al content and the annealing temperature. As-deposited coatings with a Cr:Al:B ratio close to 2:1:2 could crystallize as pure and dense Cr2AlB2 phases within the temperature range of 650–800 °C; higher annealing temperatures resulted in the decomposition of Cr2AlB2, while crystallization at lower temperatures was not evident from X-ray diffraction. As-deposited coatings with a Cr:Al:B ratio close to 3:1:3, despite containing a relatively higher Al content than required by the stoichiometry of Cr4AlB4, exhibited insufficient crystallization of Cr4AlB4 with unknown phases below 840 °C. Higher annealing temperatures resulted in the coexistence of Cr4AlB4 and CrB, indicating that achieving phase-pure and well-crystallized Cr4AlB4 coatings proved challenging, possibly due to the inevitable loss of Al during annealing. The configuration of the composite target and the substrates provides a promising strategy for fabricating phase-pure and dense Cr2AlB2 coatings.

Phase Formation Route of Cr2alc Ceramics from Cr, Al and Graphite Powders

Reactive Synthesis for Porous (Mo2/3Y1/3)2AlC Ceramics through Mo, Y, Al and Graphite Powders

Manufacturing of High Purity Cr2AlC MAX Phase Material and Its Characterization

Synthesis of Al 8 B 4 C 7 ceramic powder from Al/B 4 C/C mixtures

Preparation and Characterization of Al11cr4 Phase by Diffusion of Al/Cr Composite Film

Synthesis and Mechanical Properties of High-Purity Cr2alc Ceramic

Microstructure evolution of Cr 2 AlC MAX phase under a graphite bed between 1100 °C and 1500 °C

Al-Cr Coatings Prepared by Diffusion at Low Temperature and Its Phase Characterization

The effect of milling time and heat treatment on the synthesis of the Cr2AlC MAX phase

Thermal Stability of Bulk Zr2Al4C5 Ceramic at Elevated Temperatures

Synthesis, properties and thermal decomposition of the Ta4AlC3 MAX phase

Phase Assembly of Ti2SnC Powders

Effect of Cr7C3 on the Mechanical, Thermal, and Electrical Properties of Cr2AlC

Solid–liquid Reaction Synthesis of Layered Machinable Ti3AlC2 Ceramic

Synthesis of Cr2AlC Thin Films by Reactive Magnetron Sputtering

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

In-Situ Reaction Synthesis And Decomposition Of Ta2alc

Yttrium incorporation in Cr2AlC: On the metastable phase formation and decomposition of (Cr,Y)2AlC MAX phase thin films

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

Formation of M N +1 AX N Phases in Ti–Cr–Al–C Systems by Self-Propagating High-Temperature Synthesis

Fabrication of Cr2AlB2 and Cr4AlB4 MAB Phase Coatings by Magnetron Sputtering and Post-Annealing