Abstract:Tantalum carbide ceramics containing 0.25-3.40 wt% Al as densifying aid were prepared by hot pressing at 1900 degrees C under 30 MPa for 60 min. Effects of Al addition on densification, phase composition, microstructure and mechanical properties of the TaC-Al ceramics were investigated. Al was an effective oxygen getter which reacted with volatile oxygen impurities such as Ta2O5 on surfaces of TaC particles to form non-volatile minor phase of Al2O3 , thus slowed TaC grain growth via inhibiting the non-densifying matter transport by evaporation-condensation. When Al content was larger than the value that was needed for complete impurity reaction of 10Al + 3Ta(2)O(5) = 6Ta + 5Al(2)O(3), presence of Al liquid at high temperatures improved densification of the TaC-Al ceramics because Al liquid spread along the grain boundaries and wet the TaC grains. The TaC ceramic with 0.75, 1.50 and 3.40 wt% Al addition reached a relative density value of 91.6, 97.5 and 100%, respectively, with a similar average grain size of 3.5-4.8 mu m. Fe impurity dissolved in Al and formed Al6Fe; slight reaction of Al with TaC formed a thin layer of Ta-Al-C compound around TaC grains. The TaC ceramic with 1.50-3.40 wt% Al additions showed good Vickers hardness, Young's modulus and flexural strength in the range of 12.4-13.2 GPa, 413-479 GPa and 532 -673 MPa, respectively. Increase in oxidation resistance of TaC ceramics was observed at 600 degrees C in air with a few percentages of Al additions. (C) 2018 Elsevier B.V. All rights reserved.

In-Situ Reaction Synthesis And Decomposition Of Ta2alc

Microstructure and Properties of Bulk Ta2AlC Ceramic Synthesized by an in Situ Reaction/hot Pressing Method

Synthesis, properties and thermal decomposition of the Ta4AlC3 MAX phase

Effects of Al Addition on Densification, Microstructure and Mechanical Properties of TaC-Al Ceramics

<i>In Situ</i>Reaction Synthesis and Mechanical Properties of V<sub>2</sub>AlC

In Situ Reaction Synthesis And Mechanical Properties Of V2alc

Reactive Synthesis of Polycrystalline Ti3AlC2 and Its Sintering Behavior

Effect of 20 mol% Al addition on phase formation and mechanical properties of TaCx (x=0.5, 0.55, 0.6 and 0.7) ceramics

Solid–liquid Reaction Synthesis of Layered Machinable Ti3AlC2 Ceramic

Microstructure and mechanical properties of the spark plasma sintered Ta2C ceramics

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Combustion Synthesis and Thermal Stability of Ti3AlC2

Phase Formation Route of Cr2alc Ceramics from Cr, Al and Graphite Powders

Study on the Interface Microstructure of TaC/GCr15 Steel Surface Reinforced Layer Formed by In-Situ Reaction

Synthesis of TaB 2 -TaC nanocomposite powders by a boro-carbothermal reduction route

A synthesis method of Ti3AlC2 ceramic

Preparation of Ti3AlC2 and Ti2AlC by self-propagating high-temperature synthesis and study on the reaction mechanism

Formation mechanism of Ti3AlC2 in TiO2–Al–C/TiC systems at high temperatures

The reaction between Ti3AlC2 and Cu in the synthesis process of Cu/Tl3AlC2 composites

In Situ Reaction Synthesis, Electrical And Thermal, And Mechanical Properties Of Nb(4)Alc(3)

Experimental study on reaction synthesis of TiC in Al-Ti-C system