Microstructure–grain Orientation Relationship in Coarse Grain Nickel Cold-Rolled to Large Strain

H. S. Chen,A. Godfrey,N. Hansen,J. X. Xie,Q. Liu
DOI: https://doi.org/10.1016/j.msea.2006.07.177
2008-01-01
Abstract:The relationship between crystallographic orientation and the deformation microstructure formed during cold-rolling to high strains (up to ɛvM=4.5) has been investigated. The starting material was Ni (99.96% purity) with a coarse initial average grain size (approximately 500μm). Microstructural characterization was carried out using a combination of electron channeling contrast imaging and electron back-scatter diffraction orientation mapping. An orientation dependence of the deformation microstructure was observed even at the highest strain examined. A large increase in the average boundary misorientation is found at strains above ɛvM=1.8 for regions with the {112}〈111〉 and {123}〈634〉 orientations. This increase accompanies the structural transition from a medium strain microstructure to a high strain lamellar microstructure. In contrast, the average misorientation in regions of {110}〈112〉 orientation increases only slowly even up to the highest strain examined.
What problem does this paper attempt to address?