Abstract:In the present investigation, equiatomic CoCrFeMnNi high entropy alloy (HEA) was subjected to 80% cold rolling (as-rolled) followed by isothermal annealing treatment at 700 °C for different time periods. Microstructural characterization was performed using electron back-scattered diffraction (EBSD) and electron channeling contrast imaging (ECCI) techniques on the as-rolled and annealed samples. The as-rolled microstructure consisted of elongated grains mainly composed of strong α-fiber and weak γ-fiber textures. The as-rolled sample showed the formation of ingrain SBs in the γ-fiber grains, which served as preferential sites for grain nucleation. The annealing treatment of as-rolled samples at 700 °C cause static recovery (SRV) before 5 minutes of heat-treatment, whereas static recrystallization (SRX) was observed after 5 minutes of heat-treatment in the CoCrFeMnNi alloy samples. A faster rate of recrystallization kinetics was observed after 15 minutes of heat-treatment. The annealing treatment reduced the intensity of α-fiber and enhanced the Copper, Cube and P ({011} ) texture components. Copper components originated from coarse recrystallized grains, which were the results of localized grain growth phenomena. Unusual behavior of banded featured α-fiber grains was observed during the annealing process. These banded grains in the partially annealed samples consisted of subgrain-boundaries and showed a delayed response to recrystallization as compared to grains with other orientations. Stored energy (SE) and Taylor factor (M) calculations were also used to understand the delayed recrystallization response of the banded featured/retained deformed grains. The microhardness value of the as-rolled sample was approximately 450 Hv, which decreased to around 230 Hv for the fully recrystallized grains.

Recovery and Recrystallization as a Function of Deformed Microstructure Orientation in Coarse Grained Cold-Rolled Ni

Deformation And Annealing Textures Of Extruded And Cold Rolled Pure Ni Single Crystals Of Cube Orientation

Microstructure–grain Orientation Relationship in Coarse Grain Nickel Cold-Rolled to Large Strain

Evolution of Microstructure and Texture During Recovery and Recrystallization in Heavily Rolled Aluminum

Evolution of Orientations and Deformation Structures Within Individual Grains in Cold Rolled Columnar Grained Nickel

EBSD Analyses on Recovery and Recrystallization of High Purity Cold Rolled Nickel

Effect of cross cold rolling and annealing on microstructure and texture in pure nickel

Effects of Strain on Recrystallization of Nickel Metals and Nanometals Produced by Heavy Cold Rolling

Grain Orientation Induced Softening in Electrodeposited Gradient Nanostructured Nickel during Cold Rolling Deformation

Revealing the inhomogeneous nature of microstructure and texture evolution in the cold-rolled CoCrFeMnNi alloy during static recrystallization

Microstructure and Texture Evolution of Cu-Ni-P Alloy after Cold Rolling and Annealing

Development of the Cube Texture at Low Annealing Temperatures in Highly Rolled Pure Nickel

Recovery and Recrystallization in Commercial Purity Aluminum Cold Rolled to an Ultrahigh Strain

In-situ observations of static recrystallization and texture formation in a cold-rolled CoCrFeMnNi high entropy alloy

The Influence of Pre-Annealing on Recrystallization in Heavily Cold-Rolled Nickel

Nanostructured Aluminium - Recovery And Recrystallization

Texture and Deformation Structure Evolution During Rolling of Individual Grains of Columnar Grain Nickel

Orientation-Dependent Characteristics for Residual Grains During Hot Deformation of Nickel-Based Alloy 925

Recrystallization Texture in Nickel Heavily Deformed by Accumulative Roll Bonding

Orientation dependence of dynamic compared to static recovery in Interstitial Free steel

Grain Growth Mechanism of Lamellar-Structure High-Purity Nickel via Cold Rolling and Cryorolling during Annealing