Abstract:Polycrystalline Ni of two purities (99.967% (4N) and 99.5% (2N)) was deformed to an ultra-high strain of εvM=100 (εvM, von Mises strain) by high pressure torsion at room temperature. The 4N and 2N samples at this strain are nanostructured with an average boundary spacing of ∼100nm, a high density of dislocations and a large fraction of high angle boundaries (>15°) of 0.68–0.74, as determined by transmission electron microscopy, and 0.8–0.83, as determined by electron backscattering diffraction. The deformed samples were annealed isochronally for 1h at temperatures from 100 to 600°C, and the evolution of the structural parameters (boundary spacing, average boundary misorientation angle and the fraction of high angle boundaries), crystallographic texture and hardness were determined. Based on microstructural parameters the energy stored in the deformed state was estimated to be 14MPa and 24MPa for 4N Ni and 2N Ni, respectively. The isochronal annealing leads to a drop in hardness in three stages: a relatively small decrease at low temperatures (recovery), followed by a rapid decrease at intermediate temperatures (recrystallization) and a slow decrease at high temperature (grain growth). Both recovery and recrystallization of the 2N Ni are strongly retarded by the presence of impurities reducing the mobility of boundaries. In the recrystallization stage, changes in hardness, microstructure and texture show that the 4N Ni recrystallizes discontinuously, in spite of a large fraction of high angle boundaries in the deformed state. This finding contradicts previous experiments and theory, which suggest that recrystallization is continuous when the fraction of high angle boundaries is high. In the 2N Ni, the observations suggest that some structural coarsening (continuous recrystallization) may take place simultaneously with discontinuous recrystallization. The findings emphasize the importance of alloying, which can delay the process of recovery and recrystallization and thereby enable tailoring of the microstructure and properties through an optimized annealing treatment.

Evolution of microstructural parameters and flow stresses toward limits in nickel deformed to ultra-high strains

High Strain Monotonic Deformation-Structure And Strength

Microstructures of Nickel Deformed by High Pressure Torsion to High Strains

Microstructure Evolution Mechanisms in Nickel-Based Single Crystal Superalloys under Multiaxial Stress State

Strengthening of Nickel Deformed by High Pressure Torsion

Flow Behavior and Microstructural Evolution in Nickel During Hot Deformation

EBSD Study of Strain Dependent Microstructure Evolution During Hot Deformation of a Typical Nickel-Based Superalloy

Thermal behavior of pure Ni deformed by high pressure torsion to ultra-high strain

High Strain Rate Compressive Deformation Behavior of Nickel Microparticles

High-pressure strengthening in ultrafine-grained metals

Evolutionary Mechanisms in the Plastic Deformation of Γ'-Ni3(al, Ti)-strengthened Additively Manufactured Nickel-Based 939 Superalloys at Intermediate Temperatures

Size Effect Affected Mechanical Properties and Formability in Micro Plane Strain Deformation Process of Pure Nickel

Microstructure and Mechanical Properties of Nanostructured Metals Produced by High Strain Deformation

Deformed Metals and Alloys with a Structural Scale from 5 Nm to 100 Nm

Evolutionary mechanisms in the plastic deformation of γ'-Ni 3 (Al, Ti)-strengthened additively manufactured nickel-based 939 superalloys at intermediate temperatures

In-situ EBSD study of deformation behavior of nickel-based superalloys during uniaxial tensile tests

Evolution of Hot Processing Map and Microstructure of As-Forged Nickel-Based Superalloy During Hot Deformation

Microstructure of pure Ni subjected to high pressure torsion

Thermal Behavior of Ni (99.967% and 99.5% Purity) Deformed to an Ultra-High Strain by High Pressure Torsion

Lamellar Aspect-Ratio and Thickness-Dependent Strength-Ductility Synergy in Pure Nickel During In-Situ Micro-Tensile Loading

Flow Behaviors and Microstructural Evolutions of Nickel-Based ODS Superalloys During Hot Deformation