Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Use of Instrumented Micro-Indentation to Study the Mesoscopic Elasto-Plastic Behavior of Gh4145/Sq Superalloy During High-Temperature Cyclic Straining

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

A Study of Fatigue Mesoscopic Elasto-Plastic Properties of a Nickel-Base Superalloy by Instrumented Microindentation Measurements

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Molecular dynamics study of fatigue mechanical properties and microstructural evolution of Ni-based single crystal superalloys under cyclic loading

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses

Low cycle fatigue of a nickel based superalloy at high temperature: deformation microstructures

Anomalous Yield and Intermediate Temperature Brittleness Behaviors of Directionally Solidified Nickel-Based Superalloy

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

A combined cyclic viscoplasticity and entropy generation approach for modelling fatigue crack growth behavior of nickel-based superalloy at high temperature