Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Thermal Fatigue Behavior of Single-Crystal Superalloy

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

Thermomechanical Fatigue of Nickel-Based Single-Crystal Superalloys

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

In Situ Scanning Electron Microscopy Analysis of Effect of Temperature on Small Fatigue Crack Growth Behavior of Nickel-Based Single-Crystal Superalloy

Pt-Al bond coat dependence on the high-cycle fatigue rupture and deformation mechanisms of a fourth-generation single crystal superalloy at various temperatures

Effect of Overheating Events on Microstructure and Low-Cycle Fatigue Properties of a Nickel-Based Single-Crystal Superalloy

High temperature VHCF of a 3rd generation Ni-based single crystal superalloy with different casting pore sizes