Abstract:Single-crystal superalloy is the key material of turbine blade and hot end parts in aerospace field. The second generation nickel-based single crystal superalloy has been widely used because of its low cost and excellent high temperature properties. At present, the research on microstructure of superalloys at high temperature mainly depends on SEM and TEM observation after heating and loading experiment. However, such kind of work lacks real-time characterization capabilities. Carrying out in situ experiments has an important significance for understanding the real time deformation behavior and microstructure evolution of superalloys. Therefore, the development of an in situ high temperature (above 1000 degrees C) mechanical testing equipment for SEM faces huge challenges. In this work, high temperature tensile experiment at 1150 degrees C of a second generation single crystal nickel-based superalloy were carried out by means of a self-developed in situ heating tensile platform which can used in SEM. A high quality experimental data and serial SEM images were obtained in the course of tensile testing at 1150 degrees C. The analysis of force-displacement curve shows that the yield strength and fracture strength of the specimen are 580 and 620 MPa, respectively. The sequential SEM images during this research confirm that there is no obvious shape and size change for gamma and gamma' during the elastic deformation, and microstructure changing during plastic stage is mainly due to gamma phase widening which is parallel to the stress axis. The results show that the original micro-voids of samples are the weakness in high temperature tensile test at 1150 degrees C, the fracture direction is almost perpendicular to the stress axis, the crack propagated by passing the gamma' phase and through in the gamma phase, and ultimately, temperature and stress induced adjacent holes connection leading to the sample fracture.

Thermomechanical Fatigue of Nickel-Based Single-Crystal Superalloys

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Change in Failure Behavior and Fatigue Life of Single-Crystal Ni-Based Superalloys Under Thermomechanical Fatigue Loading

Molecular dynamics simulation of thermomechanical fatigue properties of Ni-based single crystal superalloys

Thermo-mechanical Fatigue Deformation and Fracture Mechanisms of Nickel-Based Powder Metallurgy Superalloy

Thermomechanical fatigue behavior and failure mechanism of a nickel-based directional solidification column crystal superalloy

Comparison of fatigue characteristics and failure analysis of Ni-based superalloy subjected to thermomechanical fatigue under different phase conditions

Deformation behavior and crack mechanism of a first generation single-crystal Ni-based superalloys under thermomechanical fatigue loading

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Thermo-mechanical fatigue crack growth in a nickel-based powder metallurgy superalloy

In-situ SEM study on fatigue crack behavior of a nickel-based single crystal alloy at 950 °C and 1050 °C

Anisotropic Thermomechanical Fatigue of a Nickel-Base Single-Crystal Superalloy Part I: Effects of Crystal Orientations and Damage Mechanisms

Evolution of fatigue mechanical properties and micro defects in nickel-based single crystal superalloys: A molecular dynamics research

Assessment of Thermo-Mechanical Fatigue in a Nickel-Based Single-Crystal Superalloy CMSX-4 Accounting for Temperature Gradient Effects

Investigation of in Situ 1150 Degrees C High Temperature Deformation Behavior and Fracture Mechanism of a Second Generation Single Crystal Superalloy

Investigation of damage mechanisms in thermomechanical fatigue of nickel-based single-crystal alloys

Study on Microstructure and Fatigue Properties of FGH96 Nickel-Based Superalloy

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy