Abstract:This study reports the fatigue failure mechanism at very -high -cycle fatigue (VHCF) regime of laser powder bed fusion (LPBF) GH4169 superalloy through a series of detailed microstructural characterizations, including scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron backscatter diffraction (EBSD), and energy dispersive spectrometer (EDS). Microstructural characterization of the solution and doubleaging post -treated initial material exhibits process -induced imperfections (mainly pores), as well as gamma ' , gamma '' and delta precipitates, and carbide. The fatigue tests were performed using an ultrasonic fatigue tester (20 kHz). Fatigue fracture analysis suggests there exists a competitive fatigue failure mechanism with surface flaw initiation and internal pore initiation, corresponding to high -cycle fatigue (HCF) and VHCF regime, respectively. Focused ion beam (FIB) samples taken within the fatigue initiation area (FIA) revealed grain refinement and precipitate dissolution behavior. Based on the characterization results, the fatigue crack initiation mechanism was hypothesized: During numerous cyclic loading, the mobile dislocations shear gamma ' and gamma '' precipitates, causing their dissolution and local chemical and mechanical alterations near internal pores. This enables twinning and promotes sub -grains formation. Sub -grains refine via localized continuous dynamic recrystallization (CDRX), forming a fine-grained layer that leads to crack initiation. This work reveals how precipitate dissolution contributes to VHCF crack initiation in LPBF GH4169 superalloy, highlighting the potential for extending alloy lifespan by adjusting precipitates and LPBF defects and incorporating these factors into fatigue life predictions for enhanced accuracy.

High temperature VHCF of a 3rd generation Ni-based single crystal superalloy with different casting pore sizes

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

Very high cycle fatigue of a notched Ni-based single crystal superalloy at high temperature

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

Microstructural Evolution and Formation of Fine Grains During Fatigue Crack Initiation Process of Laser Powder Bed Fusion Ni-based Superalloy

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

High-Temperature Low-Cycle Fatigue Properties of GH4169 Ni-based Superalloy

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

Low Cycle Fatigue and High Cycle Fatigue of K4750 Ni-based Superalloy at 600 °C: Analysis of Fracture Behavior and Deformation Mechanism

High-temperature high cycle fatigue performance of laser powder bed fusion fabricated Hastelloy X: Study into the microstructure and oxidation effects

A study of high cycle fatigue life and its correlation with microstructural parameters in IN713C nickel-based superalloy

Research on low‐cycle fatigue behavior of Ni‐based single crystal superalloy with shaped film cooling holes at high temperature

Microstructures' Effects on High Temperature Fatigue Failure Behavior of Typical Superalloys

Thickness debit effect of Ni-based single crystal superalloy thin-walled specimens in the VHCF regime based on a vibration fatigue test

Solidification behaviour and hot cracking susceptibility of a novel Ni-based superalloy

Thermal fatigue crack initiation and propagation behaviors of GH3230 nickel‐based superalloy

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Thermomechanical Fatigue of Nickel-Based Single-Crystal Superalloys