Abstract:After the converter steelmaking process, a considerable number of ferroalloys are needed to remove dissolved oxygen from the molten steel, but it also forms a lot of oxide inclusions that cannot be completely removed. At the same time, it increases the carbon emissions in the steel production process. After years of research, our team have developed a series of clean deoxidation technologies, including carbon deoxidation, hydrogen deoxidation, and waste plastic deoxidation of molten steel to address the aforementioned issues. In this study, thermodynamic calculations and laboratory experiments were employed to verify that carbon and hydrogen can reduce the total oxygen content in the molten steel melt to below 5 × 10 −6 and 10 × 10 −6 , respectively. An analysis of the deoxidation mechanisms and effects of polyethylene and polypropylene was also conducted. In addition, the applications of carbon deoxidation technology in different steels with the hot-state experiment and industrial production were discussed carefully. The carbon deoxidation experimental results of different steels were as follows: (1) the oxygen content of bearing steel was effectively controlled at 6.3 × 10 −6 and the inclusion number density was lowered by 74.73% compared to aluminum deoxidized bearing steel; (2) the oxygen content in gear steel was reduced to 7.7 × 10 −6 and a 54.49% reduction of inclusion number density was achieved with almost no inclusions larger than 5 μm from the average level of industry gear steels; (3) a total oxygen content of M2 high-speed steel was as low as 3.7 × 10 −6 . In industrial production practice, carbon deoxidation technique was applied in the final deoxidation stage for non-aluminum deoxidized bearing steel, and it yielded excellent results that the oxygen content was reduced to below 8 × 10 −6 and the oxide inclusions in the steel mainly consist of silicates, along with small amounts of spinel and calcium aluminate.

New steelmaking process based on clean deoxidation technology

Development and prospects of molten steel deoxidation in steelmaking process

Effect of carbon on isothermal reduction of high-strength steel oxide scale in 30%H2–N2 atmosphere

Control of oxide inclusion for low carbon and low silicon steel

Effect of Silicon–Manganese Deoxidation on Oxygen Content and Inclusions in Molten Steel

Oxide Inclusions in Aluminum-deoxidized Ultra-low CarbonSteel

Process Model for Manufacturing 400 Series Stainless Steel with Purified CO2 As an Auxiliary Oxidant and Realizing Carbon Cycle

Monitoring the oxygen removal process at the final stage of melting steel

Industrial Experiment of Technique Optimization on IF Steel in RH Degasser

Study on oxygen blowing optimisation of reducing (FeO) content in slag in EAF steelmaking process with high ratio of hot metal to scrap

Experimental Study on Decarburization and Chromium Retention in Stainless Steel Smelting with CO2 as Alternative to N2

Optimizing RH refining process to maximize cleanliness of low-carbon low-silicon Al killed steel

The Production Practice of Reducing the Oxygen Content in 42CrMo Steel

Experimental Study on Decarburization and Chromium Retention in Stainless Steel Smelting with CO <sub>2</sub> as Alternative to N <sub>2</sub>

Study on the reduction of Fe2O3 pellets by CO-CO2 and H2-H2O: Reaction kinetics and pore network model

Experimental Study on Decarburization and Chromium Retention in Stainless Steel Smelting with CO2 as Alternative to N-2

Optimization Dephosphorization Process of the Early Stage in 300t Steelmaking Converter with Top and Bottom Combined Blowing

Dephosphorization of high silicon hot metal based on double slag converter steelmaking technology

Investigation into Recycling of Iron Oxide Scale on H13 Steel by Low‐Temperature Carbothermal Reduction Method

Research on Top and Bottom Mixed Blowing CO2 in Converter Steelmaking Process

Metallurgical Effects of a Novel Tundish Refining Process for High-Strength Low-Alloy Hot-Rolled Plate Steels