Abstract:After the converter steelmaking process, a considerable number of ferroalloys are needed to remove dissolved oxygen from the molten steel, but it also forms a lot of oxide inclusions that cannot be completely removed. At the same time, it increases the carbon emissions in the steel production process. After years of research, our team have developed a series of clean deoxidation technologies, including carbon deoxidation, hydrogen deoxidation, and waste plastic deoxidation of molten steel to address the aforementioned issues. In this study, thermodynamic calculations and laboratory experiments were employed to verify that carbon and hydrogen can reduce the total oxygen content in the molten steel melt to below 5 × 10 −6 and 10 × 10 −6 , respectively. An analysis of the deoxidation mechanisms and effects of polyethylene and polypropylene was also conducted. In addition, the applications of carbon deoxidation technology in different steels with the hot-state experiment and industrial production were discussed carefully. The carbon deoxidation experimental results of different steels were as follows: (1) the oxygen content of bearing steel was effectively controlled at 6.3 × 10 −6 and the inclusion number density was lowered by 74.73% compared to aluminum deoxidized bearing steel; (2) the oxygen content in gear steel was reduced to 7.7 × 10 −6 and a 54.49% reduction of inclusion number density was achieved with almost no inclusions larger than 5 μm from the average level of industry gear steels; (3) a total oxygen content of M2 high-speed steel was as low as 3.7 × 10 −6 . In industrial production practice, carbon deoxidation technique was applied in the final deoxidation stage for non-aluminum deoxidized bearing steel, and it yielded excellent results that the oxygen content was reduced to below 8 × 10 −6 and the oxide inclusions in the steel mainly consist of silicates, along with small amounts of spinel and calcium aluminate.

Oxide Inclusions in Aluminum-deoxidized Ultra-low CarbonSteel

Revolution and Control of Fe-Al-(Mg, Ti)-O Oxide Inclusions in IF Steel during 260t BOF-RH-CC Process

Study on the thermodynamic stability and evolution of inclusions in Al–Ti deoxidized steel

TiN Inclusions Formation in Ti-Al Deoxidized Ultra-low Carbon Steel

Effect of Al-Ti complex deoxidation mode on steel cleanliness during RH refining of IF steels

Optimizing RH refining process to maximize cleanliness of low-carbon low-silicon Al killed steel

New steelmaking process based on clean deoxidation technology

Transient Behavior and Thermodynamics of Inclusions in Al-Ti-Deoxidized and Ca-Treated Steel

Control of Steel Composition and Evolution of Inclusions During Electroslag Remelting of NiCrMoV High‐Strength Steel

Evolution and Formation of Non-metallic Inclusions During Electroslag Remelting of a Heat-Resistant Steel for Ultra-supercritical Power Plants

Effect of Silicon–Manganese Deoxidation on Oxygen Content and Inclusions in Molten Steel

Impacts of Modification of Alloying Method on Inclusion Evolution in RH Refining of Silicon Steel

Control of Non-metallic Inclusion Plasticity and Steel Cleanliness for Ultrathin 18 Pct Cr-8 Pct Ni Stainless Steel Strip

Formation and Removal Mechanism of Nonmetallic Inclusions in 42CrMo4 Steel during the Steelmaking Process

Influence of Al addition on the grain boundary oxidation of Ultra High Strength Steels during hot coiling

Research status of inclusions in bearing steel and discussion on non-alloy deoxidation process

Thermodynamic features of the modifi cation of non-metallic inclusions by calcium in low-carbon steels deoxidized by aluminum

Evolution Mechanism of Oxide Inclusions in Titanium-Stabilized AISI 443 Stainless Steel

Effect of Deoxidizing and Alloying Routes on the Evolution of Non-Metallic Inclusions in 55SiCr Spring Steel

Control of oxide inclusion for low carbon and low silicon steel

Development and prospects of molten steel deoxidation in steelmaking process