Evolution of nonmetallic inclusions in 80-t 9CrMoCoB large-scale ingots during electroslag remelting process
Shengchao Duan,Min Joo Lee,Yao Su,Wangzhong Mu,Dong Soo Kim,Joo Hyun Park
DOI: https://doi.org/10.1007/s12613-024-2905-9
2024-05-29
International Journal of Minerals Metallurgy and Materials
Abstract:In combination with theoretical calculations, experiments were conducted to investigate the evolution behavior of nonmetallic inclusions (NMIs) during the manufacture of large-scale heat-resistant steel ingots using 9CrMoCoB heat-resistant steel and CaF 2 –CaO–Al 2 O 3 –SiO 2 –B 2 O 3 electroslag remelting (ESR)-type slag in an 80-t industrial ESR furnace. The main types of NMI in the consumable electrode comprised pure alumina, a multiphase oxide consisting of an Al 2 O 3 core and liquid CaO–Al 2 O 3 –SiO 2 –MnO shell, and M 23 C 6 carbides with an MnS core. The Al 2 O 3 and MnS inclusions had higher precipitation temperatures than the M 23 C 6 -type carbide under equilibrium and nonequilibrium solidification processes. Therefore, inclusions can act as nucleation sites for carbide layer precipitation. The ESR process completely removed the liquid CaO–Al 2 O 3 –SiO 2 –MnO oxide and MnS inclusion with a carbide shell, and only the Al 2 O 3 inclusions and Al 2 O 3 core with a carbide shell occupied the remelted ingot. The M 23 C 6 -type carbides in steel were determined as Cr 23 C 6 based on the analysis of transmission electron microscopy results. The substitution of Cr with W, Fe, or/and Mo in the Cr 23 C 6 lattice caused slight changes in the lattice parameter of the Cr 23 C 6 carbide. Therefore, Cr 21.34 Fe 1.66 C 6 , (Cr 19 W 4 )C 6 , Cr 18.4 Mo 4.6 C 6 , and Cr 16 Fe 5 Mo 2 C 6 can match the fraction pattern of Cr 23 C 6 carbide. The Al 2 O 3 inclusions in the remelted ingot formed due to the reduction of CaO, SiO 2 , and MnO components in the liquid inclusion. The increased Al content in liquid steel or the higher supersaturation degree of Al 2 O 3 precipitation in the remelted ingot than that in the electrode can be attributed to the evaporation of CaF 2 and the increase in CaO content in the ESR-type slag.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing