Thermodynamic and Kinetic Analysis of Non-Metallic Inclusions Evolution in Si-Killed 316L Stainless Steel with Various Refining Slags

Shengchao Duan,Taesung Kim,Jinhyung Cho,Joo Hyun Park

DOI: https://doi.org/10.1007/s12540-024-01715-8

IF: 3.451

2024-06-08

Metals and Materials International

Abstract:Reactions between Si-killed 316L stainless steel (STS316L) and CaO–SiO 2 –CaF 2 –5%MgO–5%Al 2 O 3 slag were conducted in a magnisa crucible at 1873 K to study the influences of slag binary basicity (CaO/SiO 2 ) ratio and CaF 2 content on the formation of inclusions in molten steel. Increasing the binary basicity from C/S = 1.0 to 2.3 while keeping CaF 2 content constant at 10 wt% led to a significant decrease in the total oxygen content in the molten steel. However, changing the CaF 2 content from 10 to 30 wt% had minimal impact on reducing the total oxygen content (at C/S = 1.7). The transformation of inclusions from initial SiO 2 and MnO–Cr 2 O 3 inclusions to MgO·Al 2 O 3 spinel phases and pure MgO particles occurred in the molten Si-killed STS316L when the slag had basicity values of C/S = 1.7 and 2.3, respectively. In this scenario, Al 2 O 3 inclusion could serve as an intermediary product during the mentioned transformation process. However, the utilization of slags with lower basicity (C/S = 1.0–1.3) led to the occurrence of liquid inclusions instead. The presence of Al 2 O 3 inclusions in the molten steel can be linked to the higher Al 2 O 3 activity in extremely basic slag compositions. Furthermore, the activity of MgO in high basicity and low viscosity slags (C/S = 1.7–2.3) is nearly equal to unity, causing the transfer of Mg from the slag and subsequently resulting in the transformation of inclusions from Al 2 O 3 to MgO·Al 2 O 3 and MgO inclusions under slag basicity values of 1.7 and 2.3, correspondingly, at a temperature of 1873 K. Graphical

materials science, multidisciplinary,metallurgy & metallurgical engineering