Effect of Refractory on Nonmetallic Inclusions in Si–Mn‐Killed Steel

Zhiyin Deng,Liu Cheng,Lei Chen,Miaoyong Zhu

DOI: https://doi.org/10.1002/srin.201900268

IF: 2.1258

2019-09-17

steel research international

Abstract:<p>Some laboratory experiments are carried out to study the effect of different refractories on the original and exogenous inclusions in Si‐Mn‐killed steel. It is found that, as expected, Al₂O₃ refractory would cause high melting points of both SiO₂‐Al₂O₃‐MnO system and SiO₂‐Al₂O₃‐CaO system inclusions, while MgO crucible would reduce the melting points of both systems of inclusions to a certain extent. The purity of MgO refractory is crucial for tire cord steel grades, even 0.3% of Al₂O₃ impurity in refractory would result in an evident increase (by 10%–20%) of Al₂O₃ content in the inclusions in this study. Similar to Al‐killed steel grades, MgO·Al₂O₃ spinel can also be stable in Si‐Mn‐killed steel due to the effect of MgO refractory, and MgO and Al₂O₃ inclusions would transform into MgO·Al₂O₃ spinel. These inclusions should be strictly controlled during refining process. High‐purity and high‐quality MgO refractory as well as high‐quality alloys are recommended for Si‐Mn‐killed steel grades, and Al₂O₃‐based refractory should be avoided.</p><p>This article is protected by copyright. All rights reserved.</p>

metallurgy & metallurgical engineering