Abstract:The conditions of formation of inclusions in steel during ladle refining in MgO‐C lined ladles have been investigated in laboratory experiments at 1873 K in MgO‐C crucibles with 50 g iron. From both the experimental results as well those of a thermodynamic study conducted in parallel, the following conclusions can be made about the reaction mechanism between the MgO‐C refractory and aluminium deoxidised molten steel: At steelmaking temperature an internal oxidation‐reduction occurs in the MgO‐C refractory. The formation of a thin oxide layer at the interface is due to the reaction between magnesium vapour and aluminium dissolved into the molten steel and the CO(g) generated by the reaction between MgO and C in the crucible walls. The oxide inclusions formed in the steel have been shown mainly to consist of MgO, Al2O3 or mixture of them. Some of the finest inclusions are considered to be formed as secondary inclusions during cooling and solidification of the steel and they are connected only with the diffusion of magnesium from the crucible to the molten steel. The thermodynamic calculations indicate that during vacuum refining, as the pressure decreases, the chemical compatibility of carbon‐bonded magnesia for ladle lining decreases. Die Bedingungen für die Einschlußbildung in Stahl während der sekundärmetallurgischen Behandlung in Pfannen mit MgO‐C‐Ausmauerung wurden im Labormaßstab bei 1600°C in MgO‐C‐Tiegeln mit 50g Eisen untersucht. Sowohl die Versuchsergebnisse als auch die Resultate der gleichzeitig durchgeführten thermodynamischen Studie lassen folgende Schlüsse hinsichtlich der Reaktion zwischen der MgO‐C‐Ausmauerung und dem Aluminium‐desoxidierten flüssigem Stahl zu: Bei den Stahlherstellungstemperaturen erfolgt eine Redox‐Reaktion innerhalb der MgO‐C‐Ausmauerung. Die dünne Oxidschicht an der Phasengrenze bildet sich aufgrund der Reaktion zwischen Magnesiumdämpfen und Aluminium das in der Schmelze gelöst ist, und CO(g), das aus der Reaktion von MgO und C in der Tiegelwand frei wird. Die Oxideinschlüsse, die sich im flüssigen Stahl bilden, bestehen größtenteils aus MgO·Al2O3 oder einer Mischung von den beiden. Einige der winzigen Einschlüsse sind wahrscheinlich während der Abkühlung und Erstarrung des Stahles als Sekundäreinschlüsse entstanden. Dies steht in engem Zusammenhang mit der Magnesiumdiffusion aus dem Tiegel in die Schmelze. Die thermodynamischen Berechnungen zeigen, daß die chemische Kompatibilität des kohlenstoffgebundenen MgO für die Pfannenauskleidung während der Vakuumbehandlung ‐wenn der Druckt sinkt‐ abnimmt.

Study on High‐Temperature Reactions of MgO Refractory with Ti‐Bearing Al‐Killed Steel

Reaction Mechanism between MgO and MgOC Lining Refractories and a High‐Carbon Al‐Killed Steel

Dissolution Behavior of Mg and Ca from Dolomite Refractory into Al-killed Molten Steel

Interaction Behaviors of Ce‐Treated Al‐Killed Steel Grades with Different Refractories

Dissolution Behavior of Mg from Magnesia-Chromite Refractory into Al-killed Molten Steel

Effect of Refractory on Nonmetallic Inclusions in Si–Mn‐Killed Steel

Improved properties of in-situ MgAl2O4-TiO2 dense layer reinforced low-carbon MgO-based refractories

Wetting and corrosion behavior of V– and Ti–containing slag on oxidation layer of MgO–C refractory

Elucidating the role of Ti3AlC2 and Ti3SiC2 in oxidation mechanisms of MgO–C refractories

Reaction mechanisms between slag and Ti(C,N)–MgAl2O3–Al2O3 refractories at 1600 °C

Magnesia–carbon refractory dissolution in Al killed low carbon steel

Corrosion of MgO–C Refractory with Ladle Slags

Effect of Refractory on Nonmetallic Inclusions in Al-Killed Steel

Properties of various CaO-Al2O3-TiO2 refractories and their reaction behaviours in contact with Ti6Al4V melts

Steel/refractory/slag interfacial reaction and its effect on inclusions in high-Mn high-Al steel

A study on the mechanism of reaction between refractory materials and aluminium deoxidised molten steel

Effect of Al content in molten steel on interaction between MgO–C refractory and SPHC steel

Solid reactions between CaO–Al2O3 and Si–Ti-containing steel at 1273 K

Effect of Mg addition on TiN inclusions in GCr15 bearing steel

Reaction mechanism between Al2O3–MgO refractory materials and rare earth high-carbon heavy rail steel

Dynamic interaction of refractory and molten steel: Corrosion mechanism of alumina-magnesia castables