Abstract:The metallurgical properties of blast furnace slag changed when high alumina iron ore was used extensively due to the resulting changes of the molten slag microstructure. In the study, based on typical CaO–MgO–SiO2–Al2O3 slag systems with different w(Al2O3) content, molecular dynamics simulation was used to calculate the microstructural properties of particles in the high-temperature slag system, such as bond length, partial radial distribution function, coordination numbers, and diffusion coefficient. In addition, X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and 27Al solid-state magic angle spinning nuclear magnetic resonance (27Al SS MAS NMR) were used to detect and analyze the samples. The comprehensive calculations and experimental results show that increasing w(Al2O3) can enhance the structural stability of each ion pair, and the strength of the structural stability is such that Si–O > Al–O > Mg–O > Ca–O. The self-diffusion coefficients are as follows: Mg2+ > Ca2+ > Al3+ > Si4+, which leads to the transformation of the [SiO4]4−(Q0), [Si2O7]6−(Q1) and [Si2O6]4−(Q2) structural units to [Si2O5]2−(Q3). The degree of polymerization of slag increased as well as the stability of the structural units. Moreover, the coordination of Al will change from the [AlO6]9−octahedral structure of six-coordinated Al to the [AlO5]7−pentahedral structure of five-coordinated Al and the [AlO4]5−tetrahedral structure of four-coordinated Al. It was also found that the content of non-bridge oxygen in the whole slag system decreased continuously, leading to the increasing degree of polymerization of slag, and the experimental results were consistent with the molecular dynamics calculation.

Corrosion of MgO–C Refractory with Ladle Slags

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Wetting and corrosion behavior between magnesia–carbon refractory and converter slags with different MgO contents

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Corrosion mechanism of reactive MgO‐bonded Cr2O3‐bearing castables in CaO–Al2O3–Fe2O3–SiO2‐based steel‐making slag

Research on the Wetting and Corrosion Behavior Between Converter Slag with Different Alkalinity and MgO-C Refractories

Improved slag corrosion resistance of MgO–C refractories with calcium magnesium aluminate aggregate and silicon carbide: Corrosion behavior and thermodynamic simulation

Dissolution of Al2O3–C bricks in 45 wt% CaO-45 wt% SiO2-x wt% CaF2-(10-x) wt% Na2O slag

Effect of MgO on corrosion mechanism under LF refining slag for MgAlON–MgO composites synthesized from spent MgO–C brick: Wetting behaviour, reaction process and infiltration mechanism

Corrosion mechanism of magnesia-chrome refractory bricks with FetO-SiO2-Cr2O3 copper converter slag

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Dissolution behavior of spent MgO–C refractory in the CaO–SiO2–FeO slag system as a steelmaking flux

A comparative study on the slag resistance of MgO–C, low‐carbon MgO–C, and MgO–SiC–C refractories

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Corrosion mechanism of novel MgO–Al3BC3 refractories in contact with converter slag

Corrosion mechanism of Al2O3–SiC–C refractory by SiO2–MgO-based slag

Effect of W(mgo)/w(al2o3) Ratio and Basicity on Microstructure and Metallurgical Properties of Blast Furnace Slag

Corrosion of MgO-C with Magnesium Aluminate Spinel Addition in A Steel Casting Simulator

Wetting and corrosion behavior of V– and Ti–containing slag on oxidation layer of MgO–C refractory

Corrosion Resistance of MgO and Cr2O3-Based Refractory Raw Materials to PbO-Rich Cu Slag Determined by Hot-Stage Microscopy and Pellet Corrosion Test

Numerical Understanding on Penetration and Corrosion Behavior of CaO–Al 2 O 3 –meo Slag to Al 2 O 3 –mgo Refractory