Abstract:In order to overcome the serious corrosion problem of furnace hearth refractory materials for smelting reduction ironmaking, the Cr2O3–Al2O3–MgO–ZrO2 refractories were synthesized, and the phase component, microstructure, mechanical characteristics, and slag erosion behavior of composite refractories were investigated and evaluated. The results indicate that the composite refractories mainly consist of Mg(Al, Cr)2O4 spinel phase, (Al, Cr)2O3 solid solution and ZrO2. The content of Mg (Al, Cr)2O4 spinel significantly increases with the increasing MgO content, while the content of (Al, Cr)2O3 obviously decreases. Furthermore, the comprehensive mechanical properties of the MgO modified composite refractories can be obviously enhanced by increasing the MgO content, and sample S4 presents the best mechanical characteristics when the MgO addition is 10 wt%. The corresponding hardness, compressive strength and bending strength are 14.22 GPa, 267.14 MPa and 80.0 MPa, respectively. This is mainly because the formation of Mg(Al, Cr)2O4 significantly improves the densification of composite refractories, and a large number of high-strength Mg (Al, Cr)2O4 spinel “bridge” formed between the large-sized (Al, Cr)2O3 grains. The erosion test results indicate that increasing the MgO content can significantly improve the slag infiltration resistance of composite refractories, because the formation of Mg (Al, Cr)2O4 spinel layer significantly improves the densification of MgO reinforced composite refractories. Although the slag corrosion resistance of Mg(Al, Cr)2O4 is lower than that of (Al, Cr)2O3, the Cr2O3–Al2O3–MgO–ZrO2 refractories still presents good erosion resistance, permeability resistance, and excellent mechanical characteristics.

Corrosion mechanism of Al2O3–SiC–C refractory by SiO2–MgO-based slag

Improved slag corrosion resistance of MgO–C refractories with calcium magnesium aluminate aggregate and silicon carbide: Corrosion behavior and thermodynamic simulation

Corrosion Mechanism of Alumina-Chromia Refractory by SiO2-Al2O3-CaO Based Slag from Iron Capture Process of Spent Automotive Catalyst

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Corrosion mechanism of reactive MgO‐bonded Cr2O3‐bearing castables in CaO–Al2O3–Fe2O3–SiO2‐based steel‐making slag

Research on the Wetting and Corrosion Behavior Between Converter Slag with Different Alkalinity and MgO-C Refractories

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Corrosion mechanism of novel MgO–Al3BC3 refractories in contact with converter slag

Corrosion of MgO–C Refractory with Ladle Slags

Corrosion Behavior of BF Slag to SiAlON Bonded Corundum Refractories

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Numerical Understanding on Penetration and Corrosion Behavior of CaO–Al 2 O 3 –meo Slag to Al 2 O 3 –mgo Refractory

Dissolution of Al2O3–C bricks in 45 wt% CaO-45 wt% SiO2-x wt% CaF2-(10-x) wt% Na2O slag

The critical role of aggregate microstructure in thermal shock resistance and slag resistance of Al2O3–SiC–C castable

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Effect of slag basicity on the interfacial wetting behavior between CA6 refractories and CaO–SiO2–MgO–Al2O3 based slag

Slag resistance mechanism of MgO–Mg2SiO4–SiC–C refractories containing porous multiphase aggregates

A comparative study on the slag resistance of MgO–C, low‐carbon MgO–C, and MgO–SiC–C refractories

Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier

Effect of W(mgo)/w(al2o3) Ratio and Basicity on Microstructure and Metallurgical Properties of Blast Furnace Slag

Wetting and corrosion behavior between magnesia–carbon refractory and converter slags with different MgO contents