Numerical Understanding on Penetration and Corrosion Behavior of CaO–Al 2 O 3 –meo Slag to Al 2 O 3 –mgo Refractory

Chang Liu,Guangmei Yang,Chong Tan,Guangqiang Li,Wen Yan,Zhanmin Wang,Qiang Wang

DOI: https://doi.org/10.1007/s11663-024-03042-0

2024-01-01

Abstract:To enhance the comprehension of the corrosion mechanism of refractories induced by molten slag, a 2D numerical model was developed in the present work. This model simulates the penetration of CaO–Al 2 O 3 –MeO slag into Al 2 O 3 –MgO refractory, considering capillary forces, as well as viscous and inertial resistances within the porous matrix acting on the molten slag. Experimental observations and measurements were conducted to validate the accuracy of the model. Through simulation, we visually represented the slag penetration process, highlighting the metamorphic reaction resulting from the diffusion of slag components. Notably, small aggregate particles had minimal impact on slag penetration. Instead, they were entirely enveloped by molten slag, subsequently peeling off from the refractory. The depth of penetration ( α slag = 0.05, α slag represents the volume fraction of liquid slag) exceeded three times the corrosion depth ( α slag = 0.99). Within the region penetrated by molten slag, a portion of the refractory matrix underwent metamorphosis into the liquidus phase. Significantly, reducing porosity emerged as an effective strategy to control molten slag penetration. A 44.7 pct reduction in corrosion depth was achieved by decreasing porosity from 0.28 to 0.14. This numerical model offers valuable insights into the factors influencing refractory corrosion and presents a quantitative approach for optimizing refractory designs to enhance resistance against slag penetration.