Abstract:This study investigated the local corrosion of alumina and magnesia refractory in CaO–Al 2 O 3 –SiO 2 –MgO slag due to the Marangoni effect, which is a key factor for localized wear in different industrial processes, using experimental, analytical, and numerical approaches. The objective is to explore the Marangoni effect using computational fluid dynamics simulation aiming to provide insights into the dominant slag flow patterns influencing refractory corrosion and to determine whether the observed corrosion groove can be attributed solely to the Marangoni effect. Static finger tests were conducted at temperatures of 1500 and 1550 °C employing a continuous wear testing device. A two-dimensional axisymmetrical section model of the test assembly was created, incorporating concentration-dependent surface tension gradients and surface tension forces to replicate the Marangoni flow. As the surface-tension simulation required time steps in the order of 10 −5 s, modeling up to the experimental time scale cannot be realized. Consequently, the simulation outcomes were extrapolated to anticipate the groove radii of the experimental corrosion steps. Corrosion rates were derived from measurements and analytical methodologies. Established analytical equations for corrosion under surface-tension-flows were adapted to enhance the accuracy of corrosion rate estimation. However, the analytical considerations yielded poor estimates. Meanwhile, the employed simulation model successfully generated plausible predictions of the Marangoni flow. Drawing from the extrapolated simulation outcomes, the projected groove radii exhibited a close correspondence to the measured values, demonstrating a relative error of approximately 3 %, 11 %, and 15 % for the magnesia system at 1500 °C and alumina systems at 1500 and 1550 °C, respectively. Taking into account the uncertainties inherent in the methodological approach, the disparities in the alumina values suggest the involvement of mechanisms beyond the Marangoni effect in the localized wear. Consequently, this study effectively clarifies the impact of the Marangoni effect on the local wear of the examined material systems.

Numerical Understanding on Refractory Flow-Induced Erosion and Reaction-Induced Corrosion Patterns in Ladle Refining Process

Elaboration of A Coupled Numerical Model for Predicting Magnesia Refractory Damage Behavior in High-Temperature Reactor

Numerical Understanding on Penetration and Corrosion Behavior of CaO–Al 2 O 3 –meo Slag to Al 2 O 3 –mgo Refractory

Fluid flow, slag entrainment, and composition evolution of slag inclusions during vacuum degassing refining

Dynamic interaction of refractory and molten steel: Corrosion mechanism of alumina-magnesia castables

A coupled mathematical model and experimental validation of oxygen transport behavior in the electro-slag refining process

Analysis of Temperature Losses of the Liquid Steel in a Ladle Furnace During Desulfurization Stage

Dynamic mass variation and multiphase interaction among steel, slag, lining refractory and nonmetallic inclusions: Laboratory experiments and mathematical prediction

Computational study of non-isothermal slag eye formation and its effects on ladle refining

Thickness Monitoring and Discontinuous Degradation Mechanism of Wear Lining Refractories for Refining Ladle

Experimental, analytical, and numerical quantification of the Marangoni effect in static refractory finger test

Pragmatical physics-based model for ladle lifetime prediction

Numerical Simulation of Transient Flow and Heat Transfer in a Steel Ladle During Holding Period

Thermomechanical finite element modeling of steel ladle containing alumina spinel refractory lining

Modeling of Ladle Refining Process Considering Mixing and Chemical Reaction

Quantitative Assessment of Microporous MgO Castable Erosion and Corrosion Behaviors in Two Tundish Covering Fluxes

Enhanced numerical tool to evaluate steel ladle thermal losses

Corrosion of high-chrome refractory materials by high-sodium slag in an entrained-flow gasifier

Numerical simulation on the multiphase flow and reoxidation of the molten steel in a two-strand tundish during ladle change

Refractory–Slag–Metal–Inclusion Multiphase Reactions Modeling Using Computational Thermodynamics: Kinetic Model for Prediction of Inclusion Evolution in Molten Steel

Formation of ferrospinel layer at the corroded interface between Al 2 O 3 ‐spinel refractory and molten steel in RH refining ladle