Abstract:Refractory materials used for the lining of metallurgical vessels are in direct contact with moving molten steel during the entire refining process. The dynamic interaction between molten steel and refractory material will seriously affect the service life of the refractory lining and restrict the smelting safety and efficiency of steelmaking. In this paper, experiments on the interaction between an alumina-magnesia castable and molten steel under dynamic smelting conditions were performed. The corrosion behaviour of molten steel on the alumina-magnesia refractory, which is the prevailing lining material for the refining ladle, was analysed and discussed. The corrosion mechanism of the alumina-magnesia refractory indicated that the refractory castable reacts with the molten steel and forms a metamorphic layer at the interface that has a liquid phase at high temperatures. The liquid oxide layer is emulsified with the molten steel under dynamic conditions such that the castable is eroded into the molten steel first, and steel droplets are continuously diffused into the castable and grow, which expands the scope of the reaction layer and gradually degrades the refractory castable. Consequently, the castable is peeled into the molten steel, and the molten steel is polluted. The reaction products of refractory castable and molten steel with different chemical compositions vary, and the viscosity of the reaction layer at high temperatures is the key factor. The modified capillary number (Ca*) can be used to compare the refractory wear by estimating the critical velocity of the emulsification. Furthermore, the empirical formulas for the emulsion droplet size were established, providing guidance for the application of refractory materials in the smelting of high-quality steel.

Thickness Monitoring and Discontinuous Degradation Mechanism of Wear Lining Refractories for Refining Ladle

Dynamic interaction of refractory and molten steel: Corrosion mechanism of alumina-magnesia castables

Degradation behaviors of cement-free corundum-spinel castables in Ruhrstahl Heraeus refining ladle: Role of infiltrated steel

Study On The Destroying Mechanism Of Refractory In Steel Ladle

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Numerical Understanding on Refractory Flow-Induced Erosion and Reaction-Induced Corrosion Patterns in Ladle Refining Process

Thermomechanical finite element modeling of steel ladle containing alumina spinel refractory lining

Interface Failure of Segmental Tunnel Lining Strengthened with Steel Plates Based on Fracture Mechanics

Formation of ferrospinel layer at the corroded interface between Al 2 O 3 ‐spinel refractory and molten steel in RH refining ladle

Chemical attack of Al2O3-MgAl2O4 refractory castables in the non-slag-tapping side of refining ladle

Corrosion mechanism of A508 molten steel on carbon containing refractories for steel ladle

Research on the Corrosion Behavior of Low Carbon Mold Flux on Submerged Nozzle Refractory

Numerical simulation of temperature field and thermal stress field in the new type of ladle with the nanometer adiabatic material

Slag Corrosion Behavior of Novel Lightweight Magnesia Castable in a High-Basicity Slag: Role of Micropores and Nanosized Zirconia

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Elaboration of A Coupled Numerical Model for Predicting Magnesia Refractory Damage Behavior in High-Temperature Reactor

Crack Security Influence on Refractory Design with Thermo-Mechanical Stress

Pragmatical physics-based model for ladle lifetime prediction

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Enhanced numerical tool to evaluate steel ladle thermal losses

Quantitative Assessment of Microporous MgO Castable Erosion and Corrosion Behaviors in Two Tundish Covering Fluxes