Abstract:China's 2022 crude steel production soared to an impressive 1.018 billion tons, and steel slag constituted approximately 10% to 15% of this massive output. However, a notable hindrance to the comprehensive utilization of steel slag arises from the fact that it contains 10% to 20% of free calcium oxide (f-CaO), resulting in volume instability. To address this challenge, our study delved into the dynamic transformation of the interface between lime and slag, as well as the fluctuations in the dissolution rate of lime. An Electron Probe Micro Analyzer, equipped with an energy-dispersive spectrometer, was employed for the analysis. Our findings revealed that the configuration of the reaction interface between quicklime and slag underwent alterations throughout various phases of converter smelting. At a temperature of 1400 °C, several significant transformations occurred, including the formation of a CaO-FeO solid solution, (Ca, Mg, Fe) olivine, and low-melting point (Ca, Mg) silicate minerals. With the gradual reduction in FeO content, a robust and high-melting 2CaO·SiO2 layer emerged, generated through the interaction between CaO and (Ca, Mg, Fe) olivine. Furthermore, for lime with a particle size of 20 mm and a calcination rate of 0%, the thickest layer of 2CaO·SiO2 was observed after 120 s of dissolution in slag A2 at 1400 °C. Overall, the dissolution rates of lime with different particle sizes in slag A1 to A4 showed a gradual increase. On the other hand, the dissolution rates of lime with different calcination rates in slag A1 to A4 exhibited an initial increase, followed by a decrease, and then another increase. The formation of a high-melting point and continuous dense 2CaO·SiO2 layer during the dissolution process hindered the mass transfer between lime and slag.

Dissolution behavior of spent MgO–C refractory in the CaO–SiO2–FeO slag system as a steelmaking flux

Corrosion of MgO–C Refractory with Ladle Slags

Evaluating the Effect of MgO/Al2O3 Ratio on Thermal Behaviors and Structures of Blast Furnace Slag with Low Carbon Consumption

Wetting and corrosion behavior between magnesia–carbon refractory and converter slags with different MgO contents

Dissolution Behavior of Mg from Magnesia-Chromite Refractory into Al-killed Molten Steel

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Dissolution of Carbon-Containing Species in CaO-SiO 2 -Al 2 O 3 Slag

Dissolution of Al2O3–C bricks in 45 wt% CaO-45 wt% SiO2-x wt% CaF2-(10-x) wt% Na2O slag

Dissolution Behavior of Lime with Different Properties into Converter Slag

Dissolution mechanism of magnesium aluminate spinel in copper smelting slag based on the shrinking core reaction models of corrosion

Dissolution Behavior of Mg and Ca from Dolomite Refractory into Al-killed Molten Steel

Softening–Melting Behaviors of a MgO-SiO2-FeO Slag System on a Coke Bed

Research on the Wetting and Corrosion Behavior Between Converter Slag with Different Alkalinity and MgO-C Refractories

Improved slag corrosion resistance of MgO–C refractories with calcium magnesium aluminate aggregate and silicon carbide: Corrosion behavior and thermodynamic simulation

Evolution of Interface Characteristic between Quicklime and CaO–SiO2–FetO–MgO Melt during Slag‐Forming Procedure in Converter under Different Times

A comparative study on the slag resistance of MgO–C, low‐carbon MgO–C, and MgO–SiC–C refractories

Corrosion mechanism of reactive MgO‐bonded Cr2O3‐bearing castables in CaO–Al2O3–Fe2O3–SiO2‐based steel‐making slag

Magnesia–carbon refractory dissolution in Al killed low carbon steel

Effect of unmelted lime on the element distribution behavior on a CaO-SiO2-MgO-Al2O3-FeO-CaF2(-Cr2O3) slag

Dissolution Kinetics of SiO2 into CaO-Fe2O3-SiO2 Slag

Designing low-carbon MgO–Al2O3–La2O3–C refractories with balanced performance for ladle furnaces