Calcination Condition of Dolomite‐Based Materials Influencing Static Dissolution in Synthetic Electric Arc Furnace Slag
Stefanie Lesiak,Elizaveta Cheremisina,Johannes Rieger,Johannes Schenk,Felix Firsbach,William Johnson,Thierry Chopin,Michael Nispel
DOI: https://doi.org/10.1002/srin.202100675
IF: 2.1258
2022-01-30
steel research international
Abstract:The addition of basic additives in steelmaking processes is essential because these lead to slag adaptation and enable refining reactions. In calcination treatment, the process parameters temperature and dwell time influence the decomposition of dolomite as a magnesium‐containing lime substitute. It results in specific properties such as varying residual fractions of carbonates CaCO3·MgCO3 and porosity. The properties affect the dissolution kinetics, and the fast and complete dissolution is of interest. Hence, the static high‐temperature dissolution tests using dolomite‐based samples in diverse conditions (raw, modified, soft‐burnt, and hard‐burnt) are executed to determine the impact of the calcination state. The specimens are immersed in synthetic electric arc furnace slag, including 10 wt% Al2O3, 25 wt% SiO2, 25 wt% CaO, 8 wt% MnO, and 32 wt% FeO. The dolomite or dolime dissolves in the stagnant oxidic melt within the reaction time of 10 min at 1450 °C. The resulting chemistries of quenched slags, representing the current dissolution status, are examined by scanning electron microscopy using energy‐dispersive X‐ray spectroscopy analysis on metallographically prepared cross‐sections and via X‐ray fluorescence analysis of mechanically extracted slag fractions. The dissolution performance is characterized and compared for the different additive materials. The chemical and physical properties of additives affect the dissolution behavior in slag. Applying raw dolomite, the calcination happens locally in liquid slag. Soft‐ and hard‐burnt dolime and modified materials are fabricated previously by decomposition or adjustment at high temperatures. The process conditions are used to influence the fraction of remaining carbonates and the eventual sintering of the particles.
metallurgy & metallurgical engineering