Reaction Mechanism between MgO and MgOC Lining Refractories and a High‐Carbon Al‐Killed Steel

Yujie Cheng,Wei Chen,Jujin Wang,Lifeng Zhang
DOI: https://doi.org/10.1002/srin.202400364
IF: 2.1258
2024-09-28
steel research international
Abstract:Effects of the carbon‐bonded magnesia (MgOC) refractory on the cleanliness of a high‐carbon Al‐killed steel and the refractory corrosion are investigated in comparison with the magnesia (MgO) refractory using laboratory experiments, thermodynamic calculation, and a kinetic modeling. The dissolution mechanism of the MgOC refractory in the steel are acquired. In the current study, effects of a carbon‐bonded magnesia (MgOC) refractory and a magnesia (MgO) refractory on the cleanliness of a high‐carbon Al‐killed steel and on the degree of refractory are investigated using laboratory experiments, thermodynamic calculation, and a kinetic modeling. The refractory/steel interface layer and inclusions in the steel are analyzed. After a 90 min contact between the refractory rod and the steel, the penetration of the molten steel into MgO refractory is small. An about 0.1 mm thick interface layer containing CaO–Al2O3–SiO2–MgO is generated at the boundary of magnesite particles while the composition of inclusions in the steel changes very little. The molten steel penetrated 1 mm into MgOC refractory through grain boundaries, forming channels due to the graphite consumption. A new 20 μm thick interface layer containing CaS and MgO is formed between the steel and MgOC refractory. The formation of CaS is favored at the steel/MgOC refractory and is rarely existed at the steel/MgO refractory during cooling process. The average content of MgO in inclusions increases from 6.22 to 30.05 wt% while the Al2O3 content in inclusions decreases from 84.57 to 69.95 wt% reacting for 90 min.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?