Reaction mechanisms between slag and Ti(C,N)–MgAl2O3–Al2O3 refractories at 1600 °C

Yang Sun,Yong Li,Lixin Zhang,Ling Li,Jialin Sun
DOI: https://doi.org/10.1016/j.ceramint.2020.07.276
IF: 5.532
2020-12-01
Ceramics International
Abstract:In this paper, Ti(C,N)–MgAl2O4–Al2O3 refractories were prepared by heat-treating resin bonded Al–TiO2–MgO–Al2O3 refractory at 1500 °C with N2 blowing, and the effect of Ti(C,N) on the corrosion resistance of the refractory was investigated by comparison with Al–MgO–Al2O3 refractory at 1600 °C. The results show that Ti(C,N) particles are formed in the Ti(C,N)–MgAl2O4–Al2O3 refractory by the carbon formed from resin as a precursor, which is continuously distributed in the matrix of the refractory. When the refractory is in contact with molten slag at 1600 °C, the continuously distributed Ti(C,N) absorbs [TiO2] in the slag and exists stably as Ti(C,N,O), thereby reducing the corrosion depth of the refractory. After corrosion, the boundary between the Ti(C,N)–MgAl2O4–Al2O3 refractory and the slag is clear, and the slag composition includes spinel, Ti(C,N,O) and gehlenite. Additionally, the heated Al–MgO–Al2O3 refractory shows poor corrosion resistance due to the oxidation of non-oxides such as Al4O4C and AlN.
materials science, ceramics
What problem does this paper attempt to address?