Evolution of Inclusions in Si-Mn-Killed Steel During Ladle Furnace (LF) Refining Process

Zonghui Liu,Guodong Song,Zhiyin Deng,Miaoyong Zhu

DOI: https://doi.org/10.1007/s11663-021-02074-0

2021-03-05

Metallurgical and Materials Transactions B

Abstract:<p class="a-plus-plus">To further clarify the evolution of inclusions in Si-Mn-killed steel grades, industrial samples were taken during the LF (ladle furnace) refining process, and laboratory experiments were carried out to investigate the effects of alloy additions, refining slags, and refractory materials on the evolution of inclusions. It is found that the inclusions transform along the route of "MnO-SiO<sub class="a-plus-plus">2</sub>-based inclusions → CaO-MnO-SiO<sub class="a-plus-plus">2</sub>-based inclusions → CaO-SiO<sub class="a-plus-plus">2</sub>-based inclusions", and a small amount of MgO and Al<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> are contained in these inclusions. The increase of CaO content in inclusions is generally caused by the reduction of MnO and SiO<sub class="a-plus-plus">2</sub> (especially MnO) by dissolved Ca in liquid steel, while the dissolved Al and Mg in liquid steel could also increase Al<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> and MgO in the inclusions. Both alloys and refining slag supply very limited Ca to liquid steel, which make it difficult to transform the MnO-SiO<sub class="a-plus-plus">2</sub>-based inclusions into CaO-SiO<sub class="a-plus-plus">2</sub>-based inclusions. The use of CaO-containing refractory is the main reason to cause the generation of CaO-MnO-SiO<sub class="a-plus-plus">2</sub>-based inclusions in this study, and this kind of refractory is not recommended for tire cord and saw wire steel grades.</p>