Abstract:After the converter steelmaking process, a considerable number of ferroalloys are needed to remove dissolved oxygen from the molten steel, but it also forms a lot of oxide inclusions that cannot be completely removed. At the same time, it increases the carbon emissions in the steel production process. After years of research, our team have developed a series of clean deoxidation technologies, including carbon deoxidation, hydrogen deoxidation, and waste plastic deoxidation of molten steel to address the aforementioned issues. In this study, thermodynamic calculations and laboratory experiments were employed to verify that carbon and hydrogen can reduce the total oxygen content in the molten steel melt to below 5 × 10 −6 and 10 × 10 −6 , respectively. An analysis of the deoxidation mechanisms and effects of polyethylene and polypropylene was also conducted. In addition, the applications of carbon deoxidation technology in different steels with the hot-state experiment and industrial production were discussed carefully. The carbon deoxidation experimental results of different steels were as follows: (1) the oxygen content of bearing steel was effectively controlled at 6.3 × 10 −6 and the inclusion number density was lowered by 74.73% compared to aluminum deoxidized bearing steel; (2) the oxygen content in gear steel was reduced to 7.7 × 10 −6 and a 54.49% reduction of inclusion number density was achieved with almost no inclusions larger than 5 μm from the average level of industry gear steels; (3) a total oxygen content of M2 high-speed steel was as low as 3.7 × 10 −6 . In industrial production practice, carbon deoxidation technique was applied in the final deoxidation stage for non-aluminum deoxidized bearing steel, and it yielded excellent results that the oxygen content was reduced to below 8 × 10 −6 and the oxide inclusions in the steel mainly consist of silicates, along with small amounts of spinel and calcium aluminate.

Control of oxide inclusion for low carbon and low silicon steel

Optimizing RH refining process to maximize cleanliness of low-carbon low-silicon Al killed steel

New steelmaking process based on clean deoxidation technology

Control of Steel Composition and Evolution of Inclusions During Electroslag Remelting of NiCrMoV High‐Strength Steel

Development and prospects of molten steel deoxidation in steelmaking process

Revolution and Control of Fe-Al-(Mg, Ti)-O Oxide Inclusions in IF Steel during 260t BOF-RH-CC Process

Industrial Experiment of Technique Optimization on IF Steel in RH Degasser

Effect of CaO/Al2O3 Ratio in Fluorine‐Free Refining Slag with Low Basicity on the Cleanliness of SWRS82B Steel

Cleanliness of molten steel in continuous casting tundish

Research of slagless steelmaking and technology control in converter

Effect of Silicon–Manganese Deoxidation on Oxygen Content and Inclusions in Molten Steel

Optimum Composition of Cao-Sio2-Al2o3-Mgo Slag for Spring Steel Deoxidized by Si and Mn in Production

Oxide Inclusions in Aluminum-deoxidized Ultra-low CarbonSteel

Control of Non-metallic Inclusion Plasticity and Steel Cleanliness for Ultrathin 18 Pct Cr-8 Pct Ni Stainless Steel Strip

Dephosphorization of high silicon hot metal based on double slag converter steelmaking technology

Optimizing Slag Content to Control Ds-Type Inclusions in 10B21 Cold Heading Steel

Research on Top and Bottom Mixed Blowing CO2 in Converter Steelmaking Process

Optimization of Mold Slag for Continuous Casting of Peritectic Steel

Process Improvement of Developing Cold-Rolled ULC Steel on RH

Study on oxygen blowing optimisation of reducing (FeO) content in slag in EAF steelmaking process with high ratio of hot metal to scrap

Impacts of Modification of Alloying Method on Inclusion Evolution in RH Refining of Silicon Steel