Effect of Silicon–Manganese Deoxidation on Oxygen Content and Inclusions in Molten Steel

Tianle Song,Zhongliang Wang,Yanping Bao,Chao Gu,Zefeng Zhang

DOI: https://doi.org/10.3390/pr12040767

IF: 3.5

2024-04-11

Processes

Abstract:In order to improve the cleanliness of steel, non-aluminum deoxidation processes have begun to replace aluminum deoxidation processes. Although the aluminum deoxidation process can reduce the oxygen content in steel to <10 × 10−6, this deoxidation method causes fatigue failure resulting from the formation of large-grained spherical (Ds-type) inclusions composed of calcium–aluminate. It also tends to lead to nozzle blockage during casting. Given the above problems, this study conducted an in-depth investigation of silicon–manganese deoxidation. Thermal experiments and thermodynamic calculations were used to assess the impact of different Mn–Si ratios on the oxygen content and inclusion characteristics during the deoxidation process of molten steel with different initial oxygen contents. The experimental samples were analyzed using an oxygen–nitrogen–hydrogen analyzer, a direct reading spectrometer, and an automatic scanning electron microscope. After that, the samples were electrolyzed to observe the 2D morphology and 3D morphology of the inclusions using scanning electron microscopy. Finally, thermodynamic calculations were carried out using FactSage to verify the experimental results. The results indicated that, regardless of the initial oxygen content, silicon–manganese deoxidation maintained the total oxygen content at 35 × 10−6. It effectively managed the plasticization of inclusions in molten steel, predominantly yielding spherical silicates while minimizing Al-containing inclusions. Nevertheless, as the initial content of [O] increased, the size and density of the silicate inclusions in the steel also increased. An optimal point in the number and size of inclusions was observed with an increased Mn–Si ratio. Moreover, the combined utilization of silicon–manganese deoxidation, diffusion deoxidation, and vacuum deoxidation enabled ultra-low oxygen content control of molten steel.

engineering, chemical

What problem does this paper attempt to address?

This paper aims to solve the problem of the influence of non - metallic inclusions on the quality of steel in the steel - making process, especially by replacing the traditional aluminum deoxidation process with the silicon - manganese deoxidation process to improve the purity of steel. Specifically, the paper focuses on:

1. **Reducing oxygen content**: Although the traditional aluminum deoxidation method can reduce the oxygen content in steel to below 10 × 10⁻⁶, it will lead to the formation of large - particle spherical (Ds - type) calcium aluminate inclusions. These inclusions are not plastic within the range of conventional heat - treatment temperatures and have a significant negative impact on the fatigue life of steel. In addition, aluminum deoxidation will also cause the problem of nozzle clogging during the continuous casting process. Therefore, the paper studies the influence of silicon - manganese deoxidation on the oxygen content and inclusion characteristics in steel.

2. **Improving inclusion characteristics**: Through thermodynamic experiments and thermodynamic calculations, the paper evaluates the influence of different Mn - Si ratios on the oxygen content and inclusion characteristics in molten steel. The research finds that regardless of the initial oxygen content, silicon - manganese deoxidation can maintain the total oxygen content at 35 × 10⁻⁶ and effectively manage the plastification of inclusions in molten steel, mainly generating spherical silicate inclusions while minimizing the generation of aluminum - containing inclusions.

3. **Optimizing the deoxidation process**: The paper also explores the possibility of using silicon - manganese deoxidation in combination with diffusion deoxidation and vacuum deoxidation to achieve ultra - low oxygen content control. The research results show that by optimizing the Mn - Si ratio, the number and size of inclusions can be controlled to a certain extent, thereby further improving the quality and purity of steel.

In summary, the main objective of this paper is to reduce the oxygen content and harmful inclusions in steel through the silicon - manganese deoxidation process, thereby improving the purity and performance of steel.