Control of Non-metallic Inclusion Plasticity and Steel Cleanliness for Ultrathin 18 Pct Cr-8 Pct Ni Stainless Steel Strip

Jing Guo,Shaowei Han,Xingrun Chen,Hanjie Guo,Yan Yan

DOI: https://doi.org/10.1007/s11663-020-01862-4

2020-05-26

Metallurgical and Materials Transactions B

Abstract:Laboratory-scale slag-steel equilibrium experiments as well as thermodynamic analyses and industrial tests were performed for 18 pct Cr-8 pct Ni stainless steel to study the effect of slag composition on non-metallic inclusion plasticity and steel cleanliness. First, the results showed that saturated MgO should be added in refining top slag, in particular for low-basicity slag, to avoid heavy corrosion of the refractory lining. Further, the content of MgO + Al2O3 increased and MnO content decreased in inclusions with an increase in the slag basicity; thus, the plasticity of inclusions decreased correspondingly. Conversely, higher-basicity slag was favorable for reducing the total oxygen (T.O.), while the content of dissolved aluminum (Als) in steel increased. On the basis of experimental results and thermodynamic analyses, it was concluded that comprehensive favorable inclusion plasticity and relatively high steel cleanliness could be achieved for slag basicity (CaO/SiO2) in the range of 1.4 to 1.8 and Als lower than 10 ppm. This was verified by industrial test results.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to improve the surface quality by controlling the plasticity of non - metallic inclusions and the purity of steel during the manufacturing process of ultra - thin 18% chromium - 8% nickel stainless steel strip. Specifically, the research focuses on the influence of slag composition on the plasticity of non - metallic inclusions and the purity of steel, especially the role of the basicity of slag (CaO/SiO2 ratio) and dissolved aluminum content (Als). Through laboratory - scale experiments, thermodynamic analysis and industrial tests, the author aims to find an optimal range of slag basicity to achieve favorable inclusion plasticity and high steel purity, while avoiding severe erosion of the refractory lining when using low - basicity slag.

The key findings of the paper include:
1. **The role of MgO in slag**: In order to prevent severe erosion of the refractory lining by low - basicity slag, saturated MgO needs to be added to the slag.
2. **The influence of slag basicity on inclusion plasticity**: As the basicity of slag increases, the content of MgO and Al2O3 in inclusions increases, while the content of MnO decreases, resulting in a decrease in the plasticity of inclusions. Conversely, high - basicity slag is beneficial for reducing the total oxygen (T.O.) content, but it will lead to an increase in the dissolved aluminum (Als) content in steel.
3. **The optimal range of slag basicity**: Considering the plasticity of inclusions and the purity of steel comprehensively, the basicity (CaO/SiO2) of slag should be between 1.4 and 1.8, and the Als content should be lower than 10 ppm.

These findings are of great significance for optimizing the production process of ultra - thin stainless steel strips and improving their surface quality and mechanical properties.