Abstract:Greatly enhanced hole collection of MoO x is demonstrated experimentally with a top sub-10 nm thick Ag film, allowing for an efficient dopant-free contacted crystalline silicon (c-Si) heterojunction solar cell without a front grid electrode. With the removal of shadows induced by the front grid electrode, the gridless solar cell with the MoO x /Ag hole-selective contact (HSC) shows an increment of ∼8% in its power conversion efficiency (PCE) due to the greatly improved short-circuit current density ( J sc ) as well as the almost undiminished fill factor (FF) and open-circuit voltage ( V oc ), while the gridless solar cells with the conventional MoO x /ITO and pure MoO x HSCs exhibit ∼20% and ∼43% degradations in PCE due to the overwhelming decrease in their FF and J sc , respectively. Through systematic characterizations and analyses, it is found that the ultrathin Ag film (more conductive than ITO) provides an additional channel for photogenerated holes to transport on MoO x , contributing to the great enhancement in the hole collection and the great suppression of the shunt loss in the gridless solar cells. A 50 μm thick gridless c-Si heterojunction solar cell with the MoO x /Ag HSC is 75% thinner but is 86% efficient compared to its 200 μm thick counterpart (while the 50 μm thick gridless solar cell with the MoO x /ITO HSC is much less efficient). It is over 82% efficient after being bent to a curvature radius as small as 4 mm, also showing superior mechanical flexibility to its counterpart with the MoO x /ITO HSC. Our MoO x /Ag double-layer HSC can be easily fabricated through thermal evaporation without breaking the vacuum, saving both the time and cost of the fabrication of the whole device. Therefore, this work provides a guide for the design of efficient HSCs for high-efficiency, low-cost, and flexible solar cells.

Molybdenum oxide hole selective transport layer by hot wire oxidation-sublimation deposition for silicon heterojunction solar cells

Efficient Hole Transport Layers With Widely Tunable Work Function For Deep Homo Level Organic Solar Cells

Investigation in Feasibility of Molybdenum As A Back Contact Layer for Silicon Based Quantum Dot Solar Cells

Transport mechanisms in silicon heterojunction solar cells with molybdenum oxide as a hole transport layer

Simulation of High Efficiency Silicon Heterojunction Solar Cells with Molybdenum Oxide Carrier Selective Layer

Low Oxygen Content MoOx and SiOx Tunnel Layer Based Heterocontacts for Efficient and Stable Crystalline Silicon Solar Cells Approaching 22% Efficiency

MoOx Hole Collection Layer for A-Si: H Based Photovoltaic Cells

Crystalline Silicon Heterojunction Solar Cells with Metal Oxide Window Layers

Atomic-Layer-Deposited H:MoO x Function Layer as Efficient Hole Selective Passivating Contact in Silicon Solar Cells

Heterojunction solar cells with asymmetrically carrier-selective contact structure of molybdenum-oxide/silicon/magnesium-oxide

Silicon solar cell with tunneling oxide on sulfur‐deficient intrinsic MoS2 thin film

Efficient Hole Transport Layers for Silicon Heterojunction Solar Cells by Surface Plasmonic Modification in MoOx/Au NPs/MoOx Stacks

Solution-Processed Mosx Thin-Films As Hole-Transport Layers for Efficient Polymer Solar Cells

Solution-processed vanadium oxide by low-temperature annealing for silicon solar cells with hole selective contact

Tunable Hole Selective Transport by Solution‐processed MoO3‐x Via Doping for p‐Type Crystalline Silicon Solar Cells

Annealing-Insensitive, Alcohol-Processed MoO x Hole Transport Layer for Universally Enabling High-Performance Conventional and Inverted Organic Solar Cells

Greatly enhanced hole collection of MoOx with top sub-10 nm thick silver films for gridless and flexible crystalline silicon heterojunction solar cells

Optimization of a Molybdenum Oxide Bilayer Facilitating Hole Transfer in the p/i Interface for Transparent Thin-Film Silicon Solar Cells and Modules Using Laser Scribing

Solution-processed Molybdenum Oxide Hole Transport Layer Stabilizes Organic Solar Cells

Charge trapping and photovoltaic characteristics in monocrystalline silicon solar cells employing molybdenum oxide and copper oxide stacked hole-selective contacts