Abstract:Due to native deficiency of the interfacial mismatch between Al2O3 and Al-melt, as well as micron-Al2O3 segregation at matrix grain boundaries (GBs), achieving both high strength and fracture toughness has been the long-lasting challenge for Al-CuO composite fabricated by conventional casting. Herein, we report a novel manufacturing of Al-CuO composite via shift-speed ball-milling (SSBM) of Al-5 wt.% CuO powders and afterwards subjected to hot-pressing (HP) as well as heat treatment. Comprehensive characterization shows that in-situ generation of the two types of Al2O3 with intragranular distribution, including δ*-Al2O3 particles (∼200 nm) and γ-Al2O3 whiskers (length of ∼150 nm, thickness of ∼20 nm), was governed by a diffusion-assisted nucleation-regime ascribing to the intense thermal effect of Al-CuO reaction. The size and spatial distribution of Al2O3 were emphasized to address their contribution to the high mechanical performance of the composite, which exhibits a tensile strength of ∼481 MPa and fracture elongation of ∼16.8 %. Meanwhile, the toughening mechanism of present Al-CuO composite was rationalized on basis of the "dislocation punched zone" and "plastic zone" affected by Al2O3. Both the theoretical analysis and fracture morphology support a reinforcements-matrix interface failure mechanism and the non-uniform distribution of Al2O3 consisting alternant "rich/poor zones" can markedly contribute to the high toughness. The present findings may provide a promising strategy to achieve an intragranular distribution of nano-sized reinforcements in Al-metal oxides composites, which enables increasing strength and ductility of the metal matrix.

Performance of a Hierarchically Nanostructured W–Cu Composite Produced via Mediating Phase Separation

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Nanostructured Composite Obtained by Mechanically Driven Reduction Reaction of Cuo and Al Powder Mixture

Enhancing strength-ductility properties of immiscible W-Cu composite by creating low-energy phase interfaces

Morphological Characteristics of W/Cu Composite Nanoparticles with Complex Phase Structure Synthesized via Reactive Radio Frequency (RF) Thermal Plasma

Strengthening nanocrystalline immiscible bimetallic composite by high-entropy effect

Preparation of bulk Cu-W interpenetrating-phase composites by liquid metal dealloying

Ultrahigh strength, thermal stability and high thermal conductivity in hierarchical nanostructured Cu-W alloy

Excellent wear resistance of multicomponent nanocrystalline W‒Cu based composite

PREPARATION OF ULTRAFINE W–Cu COMPOSITE POWDER USING ULTRASONIC-ASSISTED ELECTROLESS PLATING

Comparative study of the microstructure and phase evolution of FeCoCrNiAl high-entropy alloy-matrix WC nanocomposite powders prepared by mechanical alloying

Effect of Grain Refinement on the Comprehensive Mechanical Performance of W–Cu Composites

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Multiphase strengthening mechanism of Cu-Y2O3/W composites prepared by mechanical alloying

Fabrication and characterization of W/Cu/Ni-based high specific gravity alloy with Zr and Ti combined addition

Construction of a new n -body potential and multi-scale investigations of the direct alloying behaviors for immiscible W/Cu system

Revealing the strengthening and toughening mechanisms of Al-CuO composite fabricated via in-situ solid-state reaction

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Enhanced interfacial wettability and mechanical properties of Ni@Al2O3/Cu ceramic matrix composites using spark plasma sintering of Ni coated Al2O3 powders

Wear-resistance enhancement of nanostructured W-Cu-Cr composites

Fully exploiting the role of heterogeneous grain structure in graphene nanoplatelets reinforced Cu matrix composites through interfacial structure design