Abstract:In order to achieve metallurgical bonding in the form of solid solution at the Cu/W interface and avoid the formation of intermetallic compounds, the novel high entropy alloys (HEAs) were designed on the basis of the mature high entropy alloy criteria. The CuCrCoFeNi x Ti high entropy alloys interlayers were applied to weld the CuW and CuCr bimetals by sintering–infiltration technology. Scanning electron microscope, energy dispersive spectrometry, and X-ray diffraction were used to explore the interfacial microstructure evolutions and strengthening mechanism of CuW/CuCr joints with applied HEA interlayers. The interfacial characterization results show that HEAs were diffused and dissolved into bimetallic materials, and a diffusion solution layer of 2–3 μm thickness was formed at the Cu/W phase interface, and there is no new phase generated at the CuW/CuCr interface. When CuCrCoFeNi1.5Ti interlayer was infiltrated into the CuW/CuCr interface, the electrical conductivity of CuCr side is 71.6%IACS, and the interfacial tensile strength reaches 484.5 MPa. Compared with the CuW/CuCr integral material without interlayer, the interfacial bonding strength is increased by 43.1%. And the SEM fracture morphology presents a larger amount of cleavage fractures of W particles. It indicates the appropriate solid solution layer on edge of W skeletons formed at the Cu/W phases interface. The Cu/W phase interface is strengthened, and it can effectively transfer and disperse the external load. Tungsten phase with higher elastic modulus endures a large amount of load, resulting in enhancing the CuW/CuCr interfacial bonding strength. When CuCrCoFeNi2Ti high entropy alloy interlayer was applied, the W skeleton near the CuW/CuCr interface was eroded, the imperfect W skeleton cannot withstand the tensile load effectively, resulting in decrease in the CuW/CuCr interfacial bonding strength. In the interfacial fracture, appears some fragmentations of W particles, and fewer W particles occur at the cleavage fracture.

Enhancing strength-ductility properties of immiscible W-Cu composite by creating low-energy phase interfaces

Strengthening nanocrystalline immiscible bimetallic composite by high-entropy effect

Supersaturated W-Cu Nanocomposites with Outstanding Strength-Ductility Synergy

Enhancing the interface strength of additively manufactured 316 L/CuSn10 bimetallic components through heterogeneous microstructures

Improving the Interface Strength and Fatigue Property of W-Cu-steel Brazed Joint Via Induced Interface Alloying

Performance of a Hierarchically Nanostructured W–Cu Composite Produced via Mediating Phase Separation

Enhanced Ductility of W-Mo-Cu Alloy Through the Formation of Nanometer-to-micrometer-thick Dual-Phase Transition Phase Layer

Strengthening Mechanisms and Research Progress in the W/Cu Interfaces

Enhancing Metallurgical and Mechanical Properties of Friction Stir Butt Welded Joints of Al–Cu Via Cold Sprayed Ni Interlayer

Alloying mechanisms of binary immiscible systems based on tungsten-copper composite materials

Enhanced Ductility of a W-30Cu Composite by Improving Microstructure Homogeneity

Infiltrated W–Cu Composites with Combined Architecture of Hierarchical Particulate Tungsten and Tungsten Fibers

Synergetic strengthening of heterogeneous interface far beyond rule of mixture in Cu/1010 steel bimetal laminar composite

Dowel-like Morphology of Cu2Al3 Enhances Shear Strength of Interfacial Layers in Cu-Al Composites

Interface evolution and strengthening of two-step roll bonded cu/Al clad composites

Comprehensive Enhancement of the Mechanical and Thermo-Mechanical Properties of W/Cu Joints Via Femtosecond Laser Fabricated Micro/nano Interface Structures

Construction of a new n -body potential and multi-scale investigations of the direct alloying behaviors for immiscible W/Cu system

Improvement on Interfacial Properties of CuW and CuCr Bimetallic Materials with High-Entropy Alloy Interlayers Via Infiltration Method

Preparation of bulk Cu-W interpenetrating-phase composites by liquid metal dealloying

Interface evolution and strengthening of two-step roll bonded copper/aluminum clad composites

Synchronously improved mechanical strength and electrical conductivity of Carbon/Copper composites by forming Fe<sub>3</sub>C interlayer at C/Cu interface