Abstract:In this paper, excellent performance W-Cu-Ni-Fe alloys with the addition of Ni and Fe (total content: 5 wt%) were successfully prepared by low temperature liquid-phase sintering, using the raw material of ultrafine W-Cu-Ni-Fe composite powder. Ultrafine W-Cu-Ni-Fe composite powder with high sintering activity and uniform composition distribution was prepared by a two-stage reduction method consisting of carbothermal reaction and hydrogen deep deoxidation. Additions of Ni and Fe not only improved the wettability between W and Cu two phases, but also improved the bonding strength of two-phase interface. All sintered samples had higher relatively densities to ensure that the samples have great comprehensive properties. When Ni and Fe were co-added in appropriate proportions, the highest tensile strength and elongation of W-Cu-Ni-Fe alloy samples were 497 MPa and 9.12 % for the composition: W-3.5 wt%Ni-1.5 wt%Fe-25 wt%Cu, respectively. Meanwhile, with increasing Ni content from 0 wt% to 5 wt%, the compressive strength and failure strain of alloy samples increased from 1160 MPa to 2376 MPa and from 53 % to 98 %, respectively. In addition, with the enhancement of the solid solution strengthening effects of Ni and Fe on Cu matrix, the bending strength and microhardness of the alloy samples increased to 1174 MPa and 361 HV for composition: W-3.5 wt%Ni-1.5 wt%Fe-25 wt%Cu, respectively. Although the additions of Ni and Fe made the Cu matrix network structure have a uniform distribution, it led to a decrease in the electron transfer ability of the alloy, and thus, there was a decrease in electrical conductivity.

Preparation of bulk Cu-W interpenetrating-phase composites by liquid metal dealloying

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Performance of a Hierarchically Nanostructured W–Cu Composite Produced via Mediating Phase Separation

Structural characterization and mechanical properties of bicontinuous dual-metal composites prepared by liquid metal dealloying

Synthesis and mechanical properties of porous metals with inverted dealloying structure

Enhancing strength-ductility properties of immiscible W-Cu composite by creating low-energy phase interfaces

In Suit Synthesis and Bonding of Cu to W–Cu Composite by Combustion Synthesis and Centrifugal Infiltration

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Formation Mechanism of W-coated Cu Composite Powders and the Metal Injection Molding Using Polyoxymethylene-Based Binders

Alloying mechanisms of binary immiscible systems based on tungsten-copper composite materials

Construction of a new n -body potential and multi-scale investigations of the direct alloying behaviors for immiscible W/Cu system

PREPARATION OF ULTRAFINE W–Cu COMPOSITE POWDER USING ULTRASONIC-ASSISTED ELECTROLESS PLATING

Multilayered W-Cu composites with enhanced strength, electrical conductivity and wear resistance

Freeze-casted tungsten skeleton reinforced copper matrix composites

Strengthening Mechanisms and Research Progress in the W/Cu Interfaces

Additive manufacturing of W–Fe composites using laser metal deposition: Microstructure, phase transformation, and mechanical properties

Fabrication and characterization of W/Cu/Ni-based high specific gravity alloy with Zr and Ti combined addition

High-temperature mechanical and electrical properties of W-particle-reinforced Cu-matrix composites from improved electroless plated powders

Preparation and properties of W-30 wt% Cu alloy with the additions of Ni and Fe elements

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing